Steel production accounts for approximately 8% of all global CO2 emissions, with the primary steelmaking route using iron ores accounting for about 80% of those emissions, mainly due to the use of fossil-based reductants and fuel. Hydrogen-based reduction of iron oxide is an alternative for primary synthesis. However, to counteract global warming, decarbonization of the steel sector must proceed much faster than the ongoing transition kinetics in primary steelmaking. Insufficient supply of green hydrogen is a particular bottleneck. Realizing a higher fraction of secondary steelmaking thus is gaining momentum as a sustainable alternative to primary production. Steel production from scrap is well established for long products (rails, bars, wire), but there are two main challenges. First, there is not sufficient scrap available to satisfy market needs. Today, only one-third of global steel demand can be met by secondary metallurgy using scrap since many steel products have a lifetime of several decades. However, scrap availability will increase to about two-thirds of total demand by 2050 such that this sector will grow massively in the next decades. Second, scrap is often too contaminated to produce high-performance sheet steels. This is a serious obstacle because advanced products demand explicit low-tolerance specifications for safety-critical and high-strength steels, such as for electric vehicles, energy conversion and grids, high-speed trains, sustainable buildings, and infrastructure. Therefore, we review the metallurgical and microstructural challenges and opportunities for producing high-performance sheet steels via secondary synthesis. Focus is placed on the thermodynamic, kinetic, chemical, and microstructural fundamentals as well as the effects of scrap-related impurities on steel properties.@en

Metallurgical production traditionally involves three steps: extracting metals from ores, mixing them into alloys by liquid processing and thermomechanical processing to achieve the desired microstructures ^1,2. This sequential approach, practised since the Bronze Age, reaches its limit today because of the urgent demand for a sustainable economy ^2–5: almost 10% of all greenhouse gas emissions are because of the use of fossil reductants and high-temperature metallurgical processing. Here we present a H ₂-based redox synthesis and compaction approach that reforms traditional alloy-making by merging metal extraction, alloying and thermomechanical processing into one single solid-state operation. We propose a thermodynamically informed guideline and a general kinetic conception to dissolve the classical boundaries between extractive and physical metallurgy, unlocking tremendous sustainable bulk alloy design opportunities. We exemplify this approach for the case of Fe–Ni invar bulk alloys ^6,7, one of the most appealing ferrous materials but the dirtiest to produce: invar shows uniquely low thermal expansion ^6,8,9, enabling key applications spanning from precision instruments to cryogenic components ^10–13. Yet, it is notoriously eco-unfriendly, with Ni causing more than 10 times higher CO ₂ emission than Fe per kilogram production ^2,14, qualifying this alloy class as a perfect demonstrator case. Our sustainable method turns oxides directly into green alloys in bulk forms, with application-worthy properties, all obtained at temperatures far below the bulk melting point, while maintaining a zero CO ₂ footprint.

@en

Iron powder can be a sustainable alternative to fossil fuels in power supply due to its high energy density and abundance. Iron powder releases energy through exothermic oxidation (combustion), and stores back energy through its subsequent hydrogen-based reduction, establishing a circular loop for renewable energy supply. Hydrogen-based direct reduction is also gaining global momentum as possible future backbone technology for sustainable iron and steel production, with the aim to replace blast furnaces. Here, we investigate the microstructural formation mechanisms and reduction kinetics behind hydrogen-based direct reduction of combusted iron powder at moderate temperatures (400–500 °C) using thermogravimetry, ex-situ X-ray diffraction, scanning electron microscopy coupled with energy dispersive spectroscopy and electron backscatter diffraction, as well as in-situ high-energy X-ray diffraction. The influence of pre-oxidation treatment was studied by reducing both as-combusted iron powder (50 % magnetite and 50 % hematite) and the same powder after pre-oxidation (100 % hematite). A gas diffusion-limited reaction was obtained during the in-situ high-energy X-ray diffraction experiment, with successive hematite and magnetite reduction, and a strong increase in reduction kinetics with initial hematite content. Faster reduction kinetics were obtained during the thermogravimetry experiment, with simultaneous hematite and magnetite reduction. In this case, the reduction reaction was limited by a mix of phase boundary and nucleation and growth models, as analyzed by multi-step model fitting methods as well as by microstructural investigation. When not limited by gas diffusion, the pre-oxidation treatment showed almost no influence on the reduction time but a strong effect on the final microstructure of the reduced powder.

@en

Hydrogen-based direct reduction (HyDR) of iron ores has attracted immense attention and is considered a forerunner technology for sustainable ironmaking. It has a high potential to mitigate CO ₂ emissions in the steel industry, which accounts today for ~ 8–10% of all global CO ₂ emissions. Direct reduction produces highly porous sponge iron via natural-gas-based or gasified-coal-based reducing agents that contain hydrogen and organic molecules. Commercial technologies usually operate at elevated pressure, e.g., the MIDREX process at 2 bar and the HyL/Energiron process at 6–8 bar. However, the impact of H ₂ pressure on reduction kinetics and microstructure evolution of hematite pellets during hydrogen-based direct reduction has not been well understood. Here, we present a study about the influence of H ₂ pressure on the reduction kinetics of hematite pellets with pure H ₂ at 700 °C at various pressures, i.e., 1, 10, and 100 bar under static gas exposure, and 1.3 and 50 bar under dynamic gas exposure. The microstructure of the reduced pellets was characterized by combining X-ray diffraction and scanning electron microscopy equipped with electron backscatter diffraction. The results provide new insights into the critical role of H ₂ pressure in the hydrogen-based direct reduction process and establish a direction for future furnace design and process optimization. Graphical Abstract: (Figure presented.)

@en

Ammonia is a promising alternative hydrogen carrier that can be utilized for the solid-state reduction of iron oxides for sustainable ironmaking due to its easy transportation and high energy density. The main challenge for its utilization on an industrial scale is to understand the reaction kinetics under different process conditions and the associated nitrogen incorporation in the reduced material that originates from ammonia decomposition. In this work, the effect of temperature on the reduction efficiency and nitride formation is investigated through phase, local chemistry, and gas evolution analysis. The effects of inherent reactions and diffusion on phase formation and chemistry evolution are discussed in relation to the reduction temperature. The work also discusses nitrogen incorporation into the material through both spontaneous and in-process nitriding, which fundamentally affects the structure and chemistry of the reduced material. Finally, the effect of nitrogen incorporation on the reoxidation tendency of the ammonia-based reduced material is investigated and compared with that of the hydrogen-based reduced counterpart. The results provide a fundamental understanding of the reduction and nitriding for iron oxides exposed to ammonia at temperatures from 500 to 800 °C, serving as a basis for exploitation and upscaling of ammonia-based direct reduction for future green steel production.

@en

When solid-state redox-driven phase transformations are associated with mass loss, vacancies are produced that develop into pores. These pores can influence the kinetics of certain redox and phase transformation steps. We investigated the structural and chemical mechanisms in and at pores in a combined experimental-theoretical study, using the reduction of iron oxide by hydrogen as a model system. The redox product (water) accumulates inside the pores and shifts the local equilibrium at the already reduced material back toward reoxidation into cubic Fe1-xO (where x refers to Fe deficiency, space group Fm3¯m). This effect helps us to understand the sluggish reduction of cubic Fe1-xO by hydrogen, a key process for future sustainable steelmaking.

@en

Iron making is the biggest single cause of global warming. The reduction of iron ores with carbon generates about 7% of the global carbon dioxide emissions to produce ≈1.85 billion tons of steel per year. This dramatic scenario fuels efforts to re-invent this sector by using renewable and carbon-free reductants and electricity. Here, the authors show how to make sustainable steel by reducing solid iron oxides with hydrogen released from ammonia. Ammonia is an annually 180 million ton traded chemical energy carrier, with established transcontinental logistics and low liquefaction costs. It can be synthesized with green hydrogen and release hydrogen again through the reduction reaction. This advantage connects it with green iron making, for replacing fossil reductants. the authors show that ammonia-based reduction of iron oxide proceeds through an autocatalytic reaction, is kinetically as effective as hydrogen-based direct reduction, yields the same metallization, and can be industrially realized with existing technologies. The produced iron/iron nitride mixture can be subsequently melted in an electric arc furnace (or co-charged into a converter) to adjust the chemical composition to the target steel grades. A novel approach is thus presented to deploying intermittent renewable energy, mediated by green ammonia, for a disruptive technology transition toward sustainable iron making.

@en

Out of the multitude of researched processing routes for sustainable ironmaking, hydrogen-based direct reduction and hydrogen plasma smelting reduction (HyPSR) are currently the most promising candidates for a successful industrial application. Both processes operate under gaseous atmospheres, which turn the partial and absolute pressure of hydrogen into a relevant process parameter. Here, we present first insights into the influence of total pressure and concentration of hydrogen on the reduction of hematite, focusing on the more pressure-sensitive route (HyPSR). The effect of pressure on the dissociation of H2 molecules into metastable H atoms or H+ ions,- and the overall hydrogen utilization is discussed using a thermodynamic approach. Validation experiments were conducted to testify the practical feasibility of adjusting these parameters. A decrease in the total pressure of the system from 900 mbar to 450 mbar resulted in an improved hydrogen utilization, thus suggesting that a larger population of H atoms can exist in the plasma arcs ignited under 450 mbar. An increase in the hydrogen concentration to 20 vol.% lead to undesired evaporation, likely because of a parallel increase in plasma temperature. Possibilities and challenges for exploiting these pressure-related phenomena for the industrial production of green steel are outlined and discussed.@en

Hydrogen-based reduction of iron ores is the key technology for future sustainable ironmaking, to mitigate the CO2 burden from the steel industry, accounting for ~7–8% of all global emissions. However, using hydrogen as a reductant prompts concerns about hydrogen embrittlement in steel products. This raises the question of how much hydrogen remains from green ironmaking in the metal produced. We answer this question here by quantifying the amount of hydrogen in iron produced via two hydrogen-based ironmaking processes, namely, direct reduction and plasma smelting reduction. Results suggest no threat of hydrogen embrittlement resulting from using hydrogen in green steel production.@en

Steels with medium manganese (Mn) content (3∼12 wt-%) have emerged as a new alloy class and received considerable attention during the last decade. The microstructure and mechanical response of such alloys show significant differences from those of established steel grades, especially pertaining to the microstructural variety that can be tuned and the associated micromechanisms activated during deformation. The interplay and tuning opportunities between composition and the many microstructural features allow to trigger almost all known strengthening and strain-hardening mechanisms, enabling excellent strength-ductility synergy, at relatively lean alloy content. Previous investigations have revealed a high degree of microstructure and deformation complexity in such steels, but the underlying mechanisms are not adequately discussed and acknowledged. This encourages us to critically review and discuss these materials, focusing on the progress in fundamental research, with the aim to obtain better understanding and enable further progress in this field. The review addresses the main phase transformation phenomena in these steels and their mechanical behaviour, covering the whole inelastic deformation regime including yielding, strain hardening, plastic instability and damage. Based on these insights, the relationships between processing, microstructure and mechanical properties are critically assessed and rationalized. Open questions and challenges with respect to both, fundamental studies and industrial production are also identified and discussed to guide future research efforts.

@en

To successfully transition from fossil-fuel to sustainable carbon-free energy carriers, a safe, stable and high-density energy storage technology is required. The combustion of iron powders seems very promising in this regard. Yet, little is known about their in-process morphological and microstructural evolution, which are critical features for the circularity of the concept, especially the subsequent reduction of the combusted oxide powders back to iron. Here, we investigated two iron powder combustion pathways, one in air and one with the assistance of a propane pilot flame. Both processes resulted in spherical hollow particles composed of a complex microstructure of wüstite, magnetite and/or hematite. Partial evaporation is indicated by the observation of nanoparticles on the micro-sized combustion products. The associated gas production inside the liquid droplet could be the origin of the internal porosity and micro-explosion events. Cracking at the end of the combustion process results in mostly open porosity, which is favorable for the subsequent reduction process. With this study, we aim to open the perspective of iron metal fuel from macroscopic combustion analysis towards a better understanding of the underlying microscopic thermodynamic, kinetic, microstructural and thermomechanical mechanisms.

@en

Fossil-free ironmaking is indispensable for reducing massive anthropogenic CO ₂ emissions in the steel industry. Hydrogen-based direct reduction (HyDR) is among the most attractive solutions for green ironmaking, with high technology readiness. The underlying mechanisms governing this process are characterized by a complex interaction of several chemical (phase transformations), physical (transport), and mechanical (stresses) phenomena. Their interplay leads to rich microstructures, characterized by a hierarchy of defects ranging across several orders of magnitude in length, including vacancies, dislocations, internal interfaces, and free surfaces in the form of cracks and pores. These defects can all act as reaction, nucleation, and diffusion sites, shaping the overall reduction kinetics. A clear understanding of the roles and interactions of these dynamically-evolving nano-/microstructure features is missing. Gaining better insights into these effects could enable improved access to the microstructure-based design of more efficient HyDR methods, with potentially high impact on the urgently needed decarbonization in the steel industry.

@en

High-resolution three-dimensional crystal plasticity simulations are used to investigate deformation heterogeneity and microstructure evolution during cold rolling of interstitial free (IF-) steel. A Fast Fourier Transform (FFT)-based spectral solver is used to conduct crystal plasticity simulations using a dislocation-density-based crystal plasticity model. The in-grain texture evolution and misorientation spread are consistent with experimental results obtained using electron backscatter diffraction (EBSD) experiments. The crystal plasticity simulations show that two types of strain localization features develop during the large strain deformation of IF-steel. The first type forms band-like areas with large strain accumulation that appear as river patterns extending across the specimen. In addition to these river-like patterns, a second type of strain localization with rather sharp and highly localized in-grain shear bands is identified. These localized features are dependent on the crystallographic orientation of the grain and extend within a single grain. In addition to the strain localization, the evolution of in-grain orientation gradients, misorientation features, dislocation density, kernel average misorientation, and stress in major texture components are discussed.

@en

Physics-based crystal plasticity models rely on certain statistical assumptions about the collective behavior of dislocation populations on one slip system and their interactions with the dislocations on the other slip systems. One main advantage of using such physics-based constitutive dislocation models in crystal plasticity kinematic frameworks is their suitability for predicting the mechanical behavior of polycrystals over a wide range of deformation temperatures and strain rates with the same physics-based parameter set. In this study, the ability of a widely used temperature-dependent dislocation-density-based crystal plasticity formulation to reproduce experimental results, with a main focus on the yield stress behavior, is investigated. First, the material parameters are identified from experimental macroscopic stress–strain curves using a computationally efficient optimization methodology that uses a genetic algorithm along with the response surface methodology. For this purpose, a systematic set of compression tests on interstitial free (IF) steel samples is performed at various temperatures and strain rates. Next, the influence of the individual parameters on the observed behavior is analyzed. Based on mutual interactions between various parameters, the ability to find a unique parameter set is discussed. This allows identifying shortcomings of the constitutive law and sketch ideas for possible improvements. Particular attention is directed toward identifying possibly redundant material parameters, narrowing the acceptable range of material parameters based on physical criteria, and modifying the crystal plasticity formulation numerically for high-temperature use.

@en

Iron- and steelmaking cause ∼7% of the global CO ₂ emissions, due to the use of carbon for the reduction of iron ores. Replacing carbon by hydrogen as the reductant offers a pathway to massively reduce these emissions. However, the production of hydrogen using renewable energy will remain as one of the bottlenecks at least during the next two decades, because making the gigantic annual crude steel production of 1.8 billion tons sustainable requires a minimum stoichiometric amount of ∼97 million tons of green hydrogen per year. Another fundamental aspect to render the ironmaking sector more sustainable lies in an optimal utilization of green hydrogen and energy, thus reducing efforts for costly in-process hydrogen recycling. We therefore demonstrate here how the efficiency in hydrogen and energy consumption during iron ore reduction can be dramatically improved by the knowledge-based combination of two technologies: partially reducing the ore at low temperature via solid-state direct reduction (DR) to a kinetically defined degree, and subsequently melting and completely transforming it to iron under a reducing plasma (i.e. via hydrogen plasma reduction, HPR). Results suggest that an optimal transition point between these two technologies occurs where their efficiency in hydrogen utilization is equal. We found that the reduction of hematite through magnetite into wüstite via DR is clean and efficient, but it gets sluggish and inefficient when iron forms at the outermost layers of the iron ore pellets. Conversely, HPR starts violent and unstable with arc delocalization, but proceeds smoothly and efficiently when processing semi-reduced oxides, an effect which might be related to the material's high electrical conductivity. We performed hybrid reduction experiments by partially reducing hematite pellets via DR at 700 °C to 38% global reduction (using a standard thermogravimetry system) and subsequently transferring them to HPR, conducted with a lean gas mixture of Ar-10%H ₂ in an arc-melting furnace, to achieve full conversion into liquid iron. This hybrid approach allows to exploit the specific characteristics and kinetically favourable regimes of both technologies, while simultaneously showing the potential to keep the consumption of energy and hydrogen low and improve both, process stability and furnace longevity by limiting its overexposure to plasma radiation.

@en

Steel production causes a third of all industrial CO ₂ emissions due to the use of carbon-based substances as reductants for iron ores, making it a key driver of global warming. Therefore, research efforts aim to replace these reductants with sustainably produced hydrogen. Hydrogen-based direct reduction (HyDR) is an attractive processing technology, given that direct reduction (DR) furnaces are routinely operated in the steel industry but with CH ₄ or CO as reductants. Hydrogen diffuses considerably faster through shaft-furnace pellet agglomerates than carbon-based reductants. However, the net reduction kinetics in HyDR remains extremely sluggish for high-quantity steel production, and the hydrogen consumption exceeds the stoichiometrically required amount substantially. Thus, the present study focused on the improved understanding of the influence of spatial gradients, morphology, and internal microstructures of ore pellets on reduction efficiency and metallization during HyDR. For this purpose, commercial DR pellets were investigated using synchrotron high-energy X-ray diffraction and electron microscopy in conjunction with electron backscatter diffraction and chemical probing. Revealing the interplay of different phases with internal interfaces, free surfaces, and associated nucleation and growth mechanisms provides a basis for developing tailored ore pellets that are highly suited for a fast and efficient HyDR.

@en

High-entropy alloys are solid solutions of multiple principal elements that are capable of reaching composition and property regimes inaccessible for dilute materials. Discovering those with valuable properties, however, too often relies on serendipity, because thermodynamic alloy design rules alone often fail in high-dimensional composition spaces. We propose an active learning strategy to accelerate the design of high-entropy Invar alloys in a practically infinite compositional space based on very sparse data. Our approach works as a closed-loop, integrating machine learning with density-functional theory, thermodynamic calculations, and experiments. After processing and characterizing 17 new alloys out of millions of possible compositions, we identified two high-entropy Invar alloys with extremely low thermal expansion coefficients around 2 × 10-6 per degree kelvin at 300 kelvin. We believe this to be a suitable pathway for the fast and automated discovery of high-entropy alloys with optimal thermal, magnetic, and electrical properties.

@en

The reduction of iron ore with carbon-carriers is one of the largest sources of greenhouse gas emissions in the industry, motivating global activities to replace the coke-based blast furnace reduction by hydrogen-based direct reduction (HyDR). Iron oxide reduction with hydrogen has been widely investigated both experimentally and theoretically. The HyDR process includes multiple types of chemical reactions, solid state and defect-mediated diffusion (of oxygen and hydrogen species), several phase transformations, as well as massive volume shrinkage and mechanical stress buildup. However, studies focusing on the chemo-mechanical interplay during the reduction reaction influenced by microstructure are sparse. In this work, a chemo-mechanically coupled phase-field (PF) model has been developed to explore the interplay between phase transformation, chemical reaction, species diffusion, large elasto-plastic deformation and microstructure evolution. Energetic constitutive relations of the model are based on the system free energy which is calibrated with the help of a thermodynamic database. The model has been first applied to the classical core-shell (wüstite-iron) structure. Simulations show that the phase transformation from wüstite to α-iron can result in high stresses and rapidly decelerating reaction kinetics. Mechanical stresses create elastic energy in the system, an effect which can negatively influence the phase transformations, thus causing slow reaction kinetics and low metallization. However, if the elastic stress becomes comparatively high, it can shift the shape of the free energy from a double-well to a single-well case, speed up the transformation and result in a higher reduction degree compared to the low-stress double-well case. The model has been applied to simulate an experimentally characterized iron oxide specimen with its complex microstructure. The observed microstructure evolution during reduction is well predicted by the model. The simulation results also show that isolated pores in the microstructure are filled with water vapor during reduction, which can influence the local reaction atmosphere and dynamics.

@en

In conventional processing, metals go through multiple manufacturing steps including casting, plastic deformation, and heat treatment to achieve the desired property. In additive manufacturing (AM) the same target must be reached in one fabrication process, involving solidification and cyclic remelting. The thermodynamic and kinetic differences between the solid and liquid phases lead to constitutional undercooling, local variations in the solidification interval, and unexpected precipitation of secondary phases. These features may cause many undesired defects, one of which is the so-called hot cracking. The response of the thermodynamic and kinetic nature of these phenomena to high cooling rates provides access to the knowledge-based and tailored design of alloys for AM. Here, we illustrate such an approach by solving the hot cracking problem, using the commercially important IN738LC superalloy as a model material. The same approach could also be applied to adapt other hot-cracking susceptible alloy systems for AM.

@en

Iron- and steelmaking is the largest single industrial CO ₂ emitter, accounting for 6.5% of all CO ₂ emissions on the planet. This fact challenges the current technologies to achieve carbon-lean steel production and to align with the requirement of a drastic reduction of 80% in all CO ₂ emissions by around 2050. Thus, alternative reduction technologies have to be implemented for extracting iron from its ores. The hydrogen-based direct reduction has been explored as a sustainable route to mitigate CO ₂ emissions, where the reduction kinetics of the intermediate oxide product Fe _xO (wüstite) into iron is the rate-limiting step of the process. The total reaction has an endothermic net energy balance. Reduction based on a hydrogen plasma may offer an attractive alternative. Here, we present a study about the reduction of hematite using hydrogen plasma. The evolution of both, chemical composition and phase transformations was investigated in several intermediate states. We found that hematite reduction kinetics depends on the balance between the initial input mass and the arc power. For an optimized input mass-arc power ratio, complete reduction was obtained within 15 min of exposure to the hydrogen plasma. In such a process, the wüstite reduction is also the rate-limiting step towards complete reduction. Nonetheless, the reduction reaction is exothermic, and its rates are comparable with those found in hydrogen-based direct reduction. Micro- and nanoscale chemical and microstructure analysis revealed that the gangue elements partition to the remaining oxide regions, probed by energy dispersive spectroscopy (EDS) and atom probe tomography (APT). Si-enrichment was observed in the interdendritic fayalite domains, at the wüstite/iron hetero-interfaces and in the oxide particles inside iron. With proceeding reduction, however, such elements are gradually removed from the samples so that the final iron product is nearly free of gangue-related impurities. Our findings provide microstructural and atomic-scale insights into the composition and phase transformations occurring during iron ore reduction by hydrogen plasma, propelling better understanding of the underlying thermodynamics and kinetic barriers of this essential process.

@en