Early-age cracking risk induced by autogenous deformation is high for cementitious materials of low water-binder ratios. The autogenous deformation, viscoelastic properties, and stress evolution are three important factors for understanding and quantifying the early-age cracking risk. This paper systematically reviewed the experimental and modelling techniques of the three factors. It is found that the Temperature Stress Testing Machine is a unified experimental method for all these three factors, with a strain-controlled mode for stress evolution, hourly-repeated loading scheme for viscoelastic properties, and free condition for autogenous deformation. Such unified method provides basis for developing various models. By coupling a hydration model for volume fractions of hydrates, a homogenization model for upscaling of viscoelastic properties, and capillary pressure theory for self-desiccation shrinkage, a unified model directly mapping the mix design to the early-age stress can be constructed, which can help optimize the mix design to reduce the early-age cracking risk.

@en

Polyvinyl alcohol fiber reinforced engineered cementitious composite (ECC) using piezoelectric polymer film has attracted significant interest due to its energy harvesting potential. This work provides a theoretical model for evaluating the energy harvesting of bendable ECC using surface-mounted polyvinylidene fluoride (PVDF). In the mechanical part, concrete damage plasticity model based on the explicit dynamic analysis was utilized to simulate the dynamic flexural behavior of ECC beam under different dynamic loading rates. The mechanism of force transfer through the bond layer between the PVDF film and ECC specimen was simulated by a surface-surface sliding friction model wherein the PVDF film was simplified as shell element to reduce computational cost. Then, the electromechanical behavior of the piezoelectric film was simulated by a piezoelectric finite element model. A simplified model was also given for a quick calculation. The theoretical model was verified with the experimentally measured mechanical and electrical results from the literature. Finally, a parametric analysis of the effects of electromechanical parameters on the efficiency of energy harvesting was performed. The verified theoretical model can provide a useful tool for design and optimization of cementitious composite systems for energy harvesting application.@en

Auxetic cementitious cellular composites (ACCCs) exhibit desirable mechanical properties (e.g., high fracture resistance and energy dissipation), due to their unique deformation characteristics. In this study, a new type of cementitious auxetic material, referred to as peanut shaped ACCC, has been designed and subsequently architected using additive manufacturing techniques. Two peanut shaped ACCCs specimens with different pseudo-minor axes have been tested under uniaxial compression with Digital Image Correlation (DIC) to assess their compressive behavior, peak strength, Poisson's ratio, and energy dissipation capacity. Additionally, cyclic tests were conducted to investigate their compressive resilience properties, further elucidated through microstructural analysis using a digital optical microscope. The mechanical test results were also compared with those of previously developed elliptical-shaped ACCCs. Furthermore, a numerical model was used to simulate the mechanical behavior of peanut shaped ACCCs under uniaxial compression, and showed a good agreement with the experimental data. The auxetic behavior observed in peanut shaped ACCCs arises from the rotation of sections facilitated by fiber bridging at the ligament of adjacent holes within the cementitious unit cell. In comparison to elliptical-shaped ACCCs, peanut shaped ACCCs can exhibit a slightly more negative Poisson's ratio and mitigate stress concentration. The reduction of stress concentration enables peanut shaped ACCCs to dissipate substantial energy, showcasing enhanced ductility and toughness. In cyclic tests, peanut shaped ACCCs exhibit superior recoverable deformation elasticity, attributed to robust fiber bridging capacity. The exceptional mechanical properties exhibited by peanut shaped ACCCs offer a scalable solution for developing energy-absorbent and multifunctional cementitious materials for smart infrastructure.

@en

This study investigates the mechanical properties of cementitious composites with 3D-printed auxetic lattices, featuring negative Poisson's ratios (auxetic behavior) in multiple directions. These lattices were fabricated using vat photopolymerization 3D printing, and three base materials with varying stiffness and deformation capacities were analyzed to determine their impact on the composites’ mechanical behavior. To unravel the reinforcing mechanisms of multidirectional auxetic lattices, which exhibit auxetic behavior in both planar and out-of-plane directions, X-ray computed tomography (X-ray CT) was utilized to analyze composite damage evolutions under different strain levels. The micro-CT characterization reveals that auxetic lattices more effectively constrain crack growth and dissipate energy by distributing stress evenly within the cement matrix. In contrast, due to lack of lateral confinement, the non-auxetic lattice reinforced composites primarily dissipate energy through extensive crack propagation and interfacial damage, leading to lower peak strength. When strain exceeding 5%, although the confinement from the auxetic behavior diminished with crack propagation, the lattice can still maintain the composite's structural integrity, resulting in 1.7 times higher densification energy than conventional cement-based materials. These findings provide valuable insights for designing auxetic lattice-reinforced cementitious composites with enhanced load-bearing capacity and improved dissipation capabilities.

@en

The high deformation capacity of auxetic cementitious cellular composites (ACCCs) makes them promising for strain-based energy harvesting applications in infrastructure. In this study, a novel piezoelectric energy harvester (PEH) with ACCCs and surface-mounted PVDF film based on strain-induced piezoelectric mechanisms has been designed, fabricated, and experimentally tested. Furthermore, a numerical model for simulating the energy harvesting of ACCC-PVDF system undergoing repeated mechanical loading has been established and validated against the experimental data. The mechanical behavior of ACCCs was simulated by the concrete damage plasticity model during the preloading stage, which was converted to the second-elasticity model during cyclic loading stage. Based on the mechanical responses, analytical formulas for piezoelectric effects were developed to calculate the output voltage of the PVDF film. The output voltages of the ACCCs-PVDF system under different loading amplitudes and loading frequencies were assessed. The experimental results and models of the ACCCs-PVDF energy harvester lay a solid foundation for utilizing architected cementitious composites in energy harvesting applications to supply self-power electronics in infrastructure.

@en

Direct ink writing of cementitious materials can be an alternative way for creating vascular self-healing concrete by intentionally incorporating hollow channels in the cementitious matrix. In this study, a 3D-printable fibre reinforced mortar was first developed. Three groups of specimens were fabricated using direct ink writing, where the two top and bottom printing layers were printed with different printing directions. The macrostructure of the hardened specimens was studied using CT scanning. Four-point bending tests were carried out to investigate the initial flexural strength and the strength recovery after healing with injected epoxy resin. Furthermore, water permeability test was used to evaluate the healing potential of the samples. The results from CT scanning show that printing direction influences the actual volumes of hollow channels and the volume of small pores which are a consequence of the deposition process. The hollow channels of all samples were squeezed by the upper layers during the printing process, and the longitudinally printed samples were the most affected. When printing direction changes from longitudinal to transverse, the initial flexural strength decreases. Similarly, the average permeability of the cracked samples increases when the printing direction changes from longitudinal to transverse. Although the healing effectiveness regarding flexural strength is remarkable for all specimens, it was only possible to perform a single healing process as hollow channels were then blocked by the epoxy resin. The rough surface of the hollow channels is inferred to make it difficult to extract the epoxy resin out of the specimens.

@en