A novel highly compressible auxetic cementitious composite (ACC) is developed in this work. Contrary to conventional cementitious materials, such as plain concrete and fiber reinforced concrete, the ACC shows strain-hardening behavior under uniaxial compression: the stress continuously increases with strain up to approximately 40 % strain. On one hand, in the early compression stage, the ACC exhibit highly recoverable deformability of 10 % strain under cyclic loading (20 times higher than the constituent cementitious material). In addition, the ACC shows fatigue damage until the stiffness/strength and energy dissipation plateau values are reached after 500 cycles. At 2.5 % strain amplitude, the plateau stiffness/strength is approximately 120 MPa/3 MPa, while these values are only 25 MPa/1.2 MPa at 5 % strain amplitude. In contrast, the energy dissipation plateau of the ACC is independent from the amplitude and remains at 0.05 J/cm3. On the other hand, due to the strain-hardening behavior, the ACC exhibits significantly improved energy dissipation capacity compared to both the conventional cementitious materials and the auxetic frame. This behavior is achieved by a tailored composite action: integrating cementitious mortar with 3D printed thermoplastic polyurethane (TPU) auxetic frame. A rotating-square auxetic mechanism was designed for the TPU frame for the ACC to achieve the tailored cracking behavior. The horizontal ACC cells enable large deformability by enlarging the crack width under the confinement of the auxetic frame, while the vertical cells work as stiffening phase to ensure load resistance. Owing to the outstanding mechanical properties, the ACC shows great potential to be applied in engineering practice where high compressive deformability is required, for instance yielding elements for squeezing tunnel linings.

@en

This study investigates the mechanical properties of cementitious composites with 3D-printed auxetic lattices, featuring negative Poisson's ratios (auxetic behavior) in multiple directions. These lattices were fabricated using vat photopolymerization 3D printing, and three base materials with varying stiffness and deformation capacities were analyzed to determine their impact on the composites’ mechanical behavior. To unravel the reinforcing mechanisms of multidirectional auxetic lattices, which exhibit auxetic behavior in both planar and out-of-plane directions, X-ray computed tomography (X-ray CT) was utilized to analyze composite damage evolutions under different strain levels. The micro-CT characterization reveals that auxetic lattices more effectively constrain crack growth and dissipate energy by distributing stress evenly within the cement matrix. In contrast, due to lack of lateral confinement, the non-auxetic lattice reinforced composites primarily dissipate energy through extensive crack propagation and interfacial damage, leading to lower peak strength. When strain exceeding 5%, although the confinement from the auxetic behavior diminished with crack propagation, the lattice can still maintain the composite's structural integrity, resulting in 1.7 times higher densification energy than conventional cement-based materials. These findings provide valuable insights for designing auxetic lattice-reinforced cementitious composites with enhanced load-bearing capacity and improved dissipation capabilities.

@en

One particularly interesting class of mechanical metamaterials are those having a negative Poisson's ratio, which are referred to as ‘auxetics’. Because of their geometrical complexity, auxetic designs cannot always be easily created. However, Additive Manufacturing (AM) methods like material extrusion in 3D printing present the opportunity to construct auxetic structures. Nevertheless, extruded 3D printed material can be highly anisotropic. Before 3D printed auxetics manufactured through material extrusion can be used in engineering applications, it is important to generate powerful simulation tools that can reliably reproduce and foretell their mechanical characteristics irrespective of their form and intricacy. In view of this, the current work proposes printing path-dependent models based on an experimentally validated multi-scale modelling scheme using the Lattice Beam Model (LBM). This is done by first representing idealized microstructures of extruded 3D printed polymers through geometric models and simulating these on the material scale. The aim is to explicitly model the inter-layer and intra-layer bonds that exist in material extruded 3D printed parts by assigning experimentally obtained interface properties that significantly differ from the bulk material. On the auxetic structure scale, two planar auxetic designs are modelled using the determined material scale relationships as input: Re-Entrant (RE) and Rotating Square (RS). In terms of mechanical response, the experimentally and numerically obtained force displacement curves agree reasonably well: the stiffness of the modelled auxetic designs fit well with the experimentally measured ones while the LBM simulations generally provide a good estimation in strength. Finally, it has been shown on both the material and auxetic structure scales that incorporation of the interfacial bond strengths in simulations of extruded 3D printed polymers is important, because neglecting these results in significant overestimation of the strength.

@en

Due to its large number of advantages compared to traditional subtractive manufacturing techniques, additive manufacturing (AM) has gained increasing attention and popularity. Among the most common AM techniques is fused filament fabrication (FFF), usually referred to by its trademarked name: fused deposition modeling (FDM). This is the most efficient technique for manufacturing physical three-dimensional thermoplastics, such that FDM machines are nowadays the most common. Regardless of the 3D-printing methodology, AM techniques involve layer-by-layer deposition. Generally, this layer-wise process introduces anisotropy into the produced parts. The manufacturing procedure creates parts possessing heterogeneities at the micro (usually up to 1 mm) and meso (mm to cm) length scales, such as voids and pores, whose size, shape, and spatial distribution are mainly influenced by the so-called printing process parameters. Therefore, it is crucial to investigate their influence on the mechanical properties of FDM 3D-printed parts. This review starts with the identification of the printing process parameters that are considered to affect the micromechanical composition of FDM 3D-printed polymers. In what follows, their (negative) influence is attributed to characteristic mechanical properties. The remainder of this work reviews the state of the art in geometrical, numerical, and experimental analyses of FDM-printed parts. Finally, conclusions are drawn for each of the aforementioned analyses in view of microstructural modeling.@en