A new route towards strong yet ductile metals via architecting heterogeneities in both structure and metastability is presented. Such heterogeneities are generated and manipulated in a standard stainless steel using a heterogeneous phase transformation (het-PT) strategy, in which focused laser patterning is applied to stimulate site-specific phase transformations. The het-PT processed steel contains periodically arranged stripes of strong martensite and ductile austenite with different grain sizes and metastability. The resulting structural heterogeneity leads to a desirable strain gradient and heterogeneous deformation-induced martensitic transformation during deformation, which effectively accommodate strain localization and enhance work hardening capability in the het-PT-processed steel. These unique features result in an enhanced balance between strength and ductility, outperforming both homogeneously ultrafine-grained and coarse-grained counterparts. The het-PT strategy is expected to be applicable to tailoring structural heterogeneity and metastability in other steels and metals.

Over many decades, significant efforts have been made to improve the strength-elongation product of advanced high strength steels (AHSSs) by creating tailored multi-phase microstructures. Successive solid-state phase transformations for steels with a well selected chemical composition turned out to be the key instrument in the realisation of such microstructures. In this contribution, we first provide a brief review of the desired microstructures for Transformation-induced plasticity (TRIP), Carbide-free Bainitic (CFB), Quenching & Partitioning (Q&P) and Medium Manganese steels followed by comprehensive discussions on the phase transformations to be used in their creation. The implications for the steel composition to be selected are addressed too. As the presence of the right amount and type of metastable retained austenite (RA) is of crucial importance for the mechanical performance of these AHSSs, special attention is paid to the important role of successive solid-state phase transformations in creating the desired fraction and composition of RA by suitable element partitioning (in particular C and Mn). This critical partitioning not only takes place during final cooling (austenite decomposition) but also during the back transformation (austenite reversion) during reheating. This review aims to be more than just descriptive of the various findings, but to present them from a coherent thermodynamic / thermo-kinetic perspective, such that it provides the academic and industrial community with a rather complete conceptual and theoretical framework to accelerate the further development of this important class of steels. The detailed stepwise treatment makes the review relevant not only for experts but also metallurgists entering the field.

For decades, grain boundary engineering has proven to be one of the most effective approaches for tailoring the mechanical properties of metallic materials, although there are limits to the fineness and types of microstructures achievable, due to the rapid increase in grain size once being exposed to thermal loads (low thermal stability of crystallographic boundaries). Here, we deploy a unique chemical boundary engineering (CBE) approach, augmenting the variety in available alloy design strategies, which enables us to create a material with an ultrafine hierarchically heterogeneous microstructure even after heating to high temperatures. When applied to plain steels with carbon content of only up to 0.2 weight %, this approach yields ultimate strength levels beyond 2.0 GPa in combination with good ductility (>20%). Although demonstrated here for plain carbon steels, the CBE design approach is, in principle, applicable also to other alloys.