Impact behavior of auxetic cementitious cellular composites (ACCCs) architected through additive manufacturing (AM) assisted casting

Abstract

Auxetic cementitious cellular composites (ACCCs) possess advantageous mechanical properties in static tests, such as high fracture resistance and efficient energy dissipation. However, little attention has been given to understanding the impact resistance of ACCCs. In this study, two typical elliptical-shaped ACCC specimens, P25 and P50, were designed with major axis lengths increased by 25 % and 50 %, respectively, compared to the reference P0 with circular holes. The specimens were architected through additive manufacturing (AM) assisted casting, and subjected to low-velocity impacts from Schmidt hammer with a consistent initial impact energy. Their impact resistance was assessed based on impact responses, including rebound value, absorption energy, localized damage in the impact zone, crack propagation, and peak reaction force during impact. Besides single impact tests, multiple impact tests were conducted until specimens failed. Their impact results were compared with those of the reference (P0). A high-speed camera was further used for Digital Image Correlation (DIC) to analyze strain distribution of the specimens during the brief impact period. Furthermore, a numerical model considering strain rate effects was developed to simulate the impact behavior of ACCCs, demonstrating good agreement with experimental data. On this basis, a parametric analysis was performed to evaluate the effects of impact energy, relative density, specimen size, and RVE size on impact resistance. Both experimental and numerical results indicate that ACCCs demonstrate superior impact resistance compared to the reference (P0). They exhibit mitigated localized damage in the impact zone and increased contact stiffness. Moreover, ACCCs show greater endurance under multiple impacts and higher accumulated energy absorption until failure. This enhanced performance is attributed to auxetic behavior, which draws more material into the impact zone for dispersing energy and reducing localized damage, thereby maintaining overall structural integrity. Specifically, P50 exhibits higher impact resistance than P25 due to the enhanced auxetic behavior resulting from its greater aspect ratio. This creates a greater bending moment to enable more ligaments to dissipate energy through rotation-induced plastic deformation, thereby reducing localized damage. Considering the widespread availability of cementitious materials, this study highlights the potential of ACCCs for lightweight, high-performance protective structural materials for impact mitigation in infrastructure.