A compounded system of fly ash (FA) and carbide slag (CS) was proposed for CO₂ mineralization using the aqueous approach to prepare supplementary cementitious material. Influence of CS dosage on the morphology, particle size distribution, and chemical phases of the carbonation products were characterized. It is found that the mineralization products (calcite) cover on the surface of FA leading to a remarkable synergistic effect in which the CO₂ uptake is improved by about 50%. Furthermore, FA with calcite attached effectively mitigates the set retardation in OPC/FA blends by about 30% and improved the 3- and 28-day compressive strengths by 37.2% and 24.3% respectively due to combined physical and chemical effects. The results indicate that a high-volume cement replacement can be achieved using the carbonated FA produced by the proposed synergy CO₂ mineralization.

White mud is a solid waste from the papermaking industry, composed mainly of CaCO₃ and residual alkali metal ions (such as Na+, Mg²⁺). In the current study, the feasibility of using white mud as partial replacement of slag in alkali activated materials is explored. The fluidity, setting time, autogenous shrinkage, mechanical properties, hydration products and microstructure of alkali activated slag containing different amount of white mud are studied. The results show that adding white mud reduces the fluidity of freshly mixed paste, setting time and autogenous shrinkage. The ions released from the white mud participate in the polymerization reaction, accelerate the hydration reaction in the early stage, and promotes the precipitation of Mg-Al and the formation of hydrotalcite. However, excessive quantities of white mud (above 15% of the binder) leads to the reduction of compressive strength. As the content of white mud is enhanced, the Ca/(Si + Al) ratio of the gel increases and the degree of polymerization is reduced. It has been shown that white mud has potential reactivity and can partially replace slag to prepare new alkali activated materials.