A compounded system of fly ash (FA) and carbide slag (CS) was proposed for CO₂ mineralization using the aqueous approach to prepare supplementary cementitious material. Influence of CS dosage on the morphology, particle size distribution, and chemical phases of the carbonation products were characterized. It is found that the mineralization products (calcite) cover on the surface of FA leading to a remarkable synergistic effect in which the CO₂ uptake is improved by about 50%. Furthermore, FA with calcite attached effectively mitigates the set retardation in OPC/FA blends by about 30% and improved the 3- and 28-day compressive strengths by 37.2% and 24.3% respectively due to combined physical and chemical effects. The results indicate that a high-volume cement replacement can be achieved using the carbonated FA produced by the proposed synergy CO₂ mineralization.

@en

An engineered cementitious composite (ECC) belongs to a type of high-performance fiber-reinforced materials. Fiber alignment causes the anisotropy of such materials. Herein, the influence of the fiber orientation on water and ion penetration into an ECC was studied. Fiber alignment was achieved using an extrusion approach. Water absorption, sorptivity, chloride penetration resistance, sulfate attack resistance, and freezing–thawing resistance of specimens with fiber aligned horizontally (AH), vertically (AV), and randomly (R), corresponding to the direction of the exposure surface that was studied. The results showed that fibers oriented perpendicular to the water path delayed water migration into the ECC matrix. The sorptivity was significantly affected by the fiber direction. The sorptivity of the AH specimens was 35% and 13% lower than that of the AV and R specimens, respectively. After 180 days of exposure, the chloride penetration depth of the AH specimens was 5.7 mm, which is 13.6% and 20.8% lower than that of the AV and R specimens, respectively. The sulfate ingress profile indicates that the fiber–matrix interface oriented perpendicular to the penetration path can effectively delay sulfate migration. The fiber orientation also influences the compressive strength gain under immersion conditions (Na2SO4 solution, Na2SO4 + NaCl solution, and water). Compared with the AH and R specimens, the AV specimens are more sensitive to the immersion condition. In contrast, the fiber orientation has no significant effect on ECC specimens under freeze–thaw cycles. These findings indicate that controlling the fiber alignment and orientation in an ECC can improve its durability under certain exposure conditions.@en

Engineered cementitious composites (ECCs) belong to a broad class of fibre-reinforced concrete. They incorporate synthetic polyvinyl alcohol (PVA) fibres, cement, fly ash and fine aggregates, and are designed to have a tensile strain capacity typically beyond 3%. This paper presents an investigation on the carbonation behaviour of engineered cementitious composites (ECCs) under coupled sustained flexural load and accelerated carbonation. The carbonation depth under a sustained stress level of 0, 0.075, 0.15, 0.3 and 0.6 relative to flexural strength was measured after 7, 14 and 28 days of accelerated carbonation. Thermogravimetric analysis, mercury intrusion porosimetry and microhardness measurements were carried out to show the coupled influence of sustained flexural load and accelerated carbonation on the changes of the mineral phases, porosity, pore size distribution and microhardness along the carbonation profile. A modified carbonation depth model that can be used to consider the coupled effect of flexural tensile stress and carbonation time was proposed. The results show that an exponential relationship can be observed between stress influence coefficient and flexural tensile stress level in the carbonation depth model of ECC, which is different when using plain concrete. Areas with a higher carbonation degree have greater microhardness, even under a large sustained load level, as the carbonation process refines the pore structure and the fibre bridges the crack effectively.

@en