With the increased deployment of power modules in demanding conditions, sintering materials, especially composite sintering materials, have raised growing interest due to their cost-effectiveness and suitability. Therefore, this study explores the viability of Cu–Ag composite sintering material, focusing on solvent influence through microstructure and mechanical behavior analysis. Micron-sized particle-based Cu–Ag composite pastes were designed and compared using eight solvents (four epoxy-free and four epoxy-added) based on fluidity and thermal stability. The sintered joints' performance, assessed through shear strength analysis, showed comparable values to pure silver sintering for both epoxy-free and epoxy-added samples. Optimized samples from each solvent system underwent reliability analysis, demonstrating that Cu–Ag joints with epoxy resin exhibited significantly higher shear strength after high-temperature storage and thermal cycling tests. Micromorphology and elemental composition analysis revealed differences in aging mechanisms, primarily attributed to variations in porosity due to oxide formation and pore filling by epoxy resin under different solvent systems. Further nanoindentation characterization of micromechanical properties, including hardness, modulus, and creep properties, during high-temperature aging, established constitutive models for insights into reliability evolution. In conclusion, the optimized epoxy-added Cu–Ag sintered joints proposed in this study demonstrated exceptional reliability and acceptable micromechanical properties, presenting a promising option for high-temperature power packaging.

@en

In the rapidly evolving era of information and intelligence,microelectronic devices are pivotal across various fields, such as mobile devices, big data computing, electric vehicles, and aerospace. However, the electrical performance of these devices often suffers due to residual stress from microelectronic manufacturing. This issue is compounded by the additional thermal stress that accumulates during device operation. Therefore, it is essential to understand, characterize, and control this residual stress to ensure the reliability and efficiency of microelectronic devices. Raman spectroscopy emerges as an invaluable tool for nondestructive, fast, noncontact, and precise testing of micro-scale mechanics, significantly aiding in stress and strain analysis within microelectronic manufacturing. This article aims to provide a thorough overview of the theory and application beyond a mere compilation of recent advances. Theoretically, it critically evaluates existing models that describe the Raman-stress relation. Practically, it explores the application of Raman spectroscopy in researching residual stress in various components, including substrate materials, epitaxial films, and packaging. Through a detailed examination of current applications, it highlights the significance of Raman spectroscopy in understanding micro-scale mechanics. Finally, it offers both theoretical and practical insights into the future developments of Raman-stress detection technology.@en

The power semiconductor joining technology through sintering of copper nanoparticles is well-suited for die attachment in wide bandgap (WBG) semiconductors, offering high electrical, thermal, and mechanical performances. However, sintered nanocopper will be prone to degradation resulting from corrosion in sulfur-containing corrosive environments such as offshore areas. In this study, experiments, including aging test and corrosion characterization, and simulations based on density functional theory (DFT) studies were conducted to explore the corrosion behavior and mechanism of elemental sulfur (S₈) and hydrogen sulfide (H₂S) on sintered nanocopper. The experimental results indicated that loose corrosion products were observed on the sintered nanocopper during the ageing process involving S₈, and compact layered corrosion products formed during the ageing process involving H₂S. Furthermore, similar corrosion product compositions (Cu₂O, Cu₂S, CuO, CuS, and potentially Cu₂SO₄ or CuSO₄) were observed in both the S₈- and H₂S-ageing processes. However, the S₈-ageing process exhibited more noticeable corrosion penetration. This was explained in simulations results: the unsaturated Cu sites on the oxide layer [Cu₂O(1 1 1)] of the sintered nanocopper could adsorb both H₂S and S₈, while the saturated Cu sites only exhibited the potential to adsorb S₈.

@en

With the popularization of wide band-gap power modules in offshore wind power systems and water surface photovoltaic power stations, packaging materials face challenges of corrosion by salt, blended with high humidity. Copper-silver (Cu-Ag) composite sintered paste was proposed by researchers as a novel die-attach material for a lower cost and anti-electro migration ability. However, the potential difference between copper and silver forms galvanic corrosion in a high-humidity environment, resulting in accelerated failure combined with salt mist. To further promote the application of composite sintered materials, a copper-silver double-sphere galvanic corrosion model based on finite element simulation was proposed in this paper. The relationship between corrosion rate and time of different Cu-Ag particle size combinations under different sintering degrees was predicted by initial exchange current density. Through the electrochemical characterization of the sintered samples, the optimal combination of materials was further discussed. The accuracy of the model was also verified. The conclusions obtained from both the experiments and simulation work provide guidance for future anti-corrosion analysis, as well as the reliability improvement of novel composite sintered materials.

@en

Power modules applied in offshore applications are facing risks of corrosion failures on die-attach materials due to high humidity and H₂S exposure. To investigate such corrosion behavior for sintered die-attach materials, we conducted a study with four groups of samples fabricated using copper and silver metal particles under different solvent systems. Such samples were firstly subjected to high-humidity-H₂S conditions for 168 h to simulate the harsh offshore environment. After undergoing corrosion, the primary compounds formed were CuO/Cu₂O and Ag₂S through SEM, XRD, and XPS analysis. Notably, the incorporation of epoxy resin into sintered copper joints resulted in a remarkable reduction in corrosion and a substantial improvement in electrical conductivity after the reaction. In contrast, while the addition of epoxy did not evidently reduce corrosion in silver joints, it did lead to a significant increase in shear strength. Furthermore, to gain further insights into the effect of epoxy resin on corrosion behavior, electrochemical analysis, and molecular dynamics simulations were conducted. Finally, the mechanical reliability of the corroded copper and silver joints was evaluated through thermal shock tests. In summary, sintered copper joints exhibited better anti-corrosion behaviors than sintered silver under high humidity and H₂S exposure, especially with the addition of epoxy resin. However, the corrosion products of sintered copper suffered from a sharp decrease in shear strength after thermal shock tests than sintered silver, which is probably due to the coefficient of thermal expansion mismatch.

@en