Solid waste sorting is an important pre-treatment in recycling to improve the efficiency of material recovery and reduce costs. Motivated by the PEACOC project on metal recovery from solid wastes, an innovative magnetic density separation (MDS) process has been developed for solid waste sorting. It has intrinsic advantages over conventional gravity separation technologies and the previously industrialized MDS process. The new MDS process applies an inclined planar magnet and a horizontal basin containing a static magnetic fluid as the separation medium. A particle sliding phenomenon is identified as a feature that could help the separation. Experiments have been carried out to demonstrate the role of the MDS in concentrating valuable metals in shredded PCBAs and reducing metallic contaminants in plastic fractions of shredded wires. A pilot scale facility is introduced to show the design to achieve continuous production and to reduce the consumption of ferrofluid.@en

Ionic rare earth ore is a type of featured rare earth ore in China. Its mining process suffers from a long leaching cycle and considerable consumption of leaching agents. Improving mining efficiency requires a sound physical understanding of the leaching process. In this study, the CFD-based numerical model is used to analyze the physical process of leaching through porous media formed by particles. The simulation results indicate that a lower packing porosity and smaller particles packed granular porous medium result in much larger energy dissipation during seepage, and the energy dissipation increases with seepage velocity. It is found that when the seepage velocity increases to a certain high value, the energy dissipation exceeds the value predicted by Darcy’s law, which is mainly caused by liquid turbulence. Additionally, the effect of particle shape is examined. The results show that the granular medium composed of prolate particles causes larger energy dissipation than oblate particles, and spherical particles play the least role. This phenomenon may result from the particle shape affecting the area of the frontal contact surface between particles and liquid. The results provide new insights into the fundamental understanding of percolation and seepage behaviors in the ion-adsorption-type rare earth ore leaching process.@en

Powder bed fusion additive manufacturing has been applied to the fabrication of functionally graded materials. A new design that allows the material composition to change along the direction perpendicular to the powder spreading has been reported in the literature. Based on this design, this work examines the quality of the graded spread powder layer with two powders, which have a large difference of density. The results reveal that during the spreading of graded powders, the volume of particles on the heavy powder side is deposited less than that on the light powder side, indicating that heavy particles diffuse to the light powder side. This diffusion is affected by the spreading speed, but not much by the layer gap. Large spreading speed causes more significant deviation. The results also show that particle size affects diffusion, indicating that decreasing the particle size of the heavy powder may be a solution to reduce diffusion. [Figure not available: see fulltext.]

@en

Understanding and controlling the composition segregation during powder spreading is of key importance in the additive manufacturing (AM) of composite materials. Under this circumstance, the segregation behavior of WC/316 L composite powders during spreading in laser powder bed fusion (LPBF) AM was numerically investigated by the discrete element method. The effects of process conditions (i.e., spreader velocity and geometry) and powder properties (i.e., size and shape of the WC powder) on the powder bed composition segregation and related characteristics were systematically analyzed. Corresponding mechanisms were identified from microscopic scale in terms of particle velocity, motion trajectory, mechanical behavior, and energy information. Finally, proper solutions in designing and constructing WC/316 L composite materials with desired gradient structures were proposed. The results show that the small blade velocity (V) will enhance the negative segregation, increase the average packing density ρ¯, and decrease uniformity ρ_vc in the WC/316 L composite powder bed. Compared with the blade, the roller can increase the negative segregation (Se_roller = −0.027 < Se_blade = −0.019) and the average packing density (ρ¯_roller = 0.31>ρ¯_blade = 0.20). When the WC/316 L size ratio increases from 25 μm/45 μm to 45 μm/45 μm, the negative segregation becomes weaker, and its value increases from −0.084 to −0.007. When the size ratio increases to 65 μm/45 μm, the powder behaves positive segregation with Se_max = 0.017; in this case, the packing density is the lowest (0.14), and the uniformity is the worst (0.17). In comparison with spherical shape, polyhedral WC powder can reduce the negative segregation of the powder bed (Se_sphere = −0.019 < Se_polyhedron = −0.008), while the WC shape has less effect on the packing density and uniformity. The density difference of the WC and 316 L powders leads to the difference in energy and force, resulting in different motion and segregation behaviors in the composite powder bed. For WC/316 L composite powder with a fixed composition, the condition of V = 0.025 m/s, WC/316 L size ratio = 25 μm/45 μm, roller spreader, and spherical WC can realize the proper composition gradient along the spreading direction in the composite powder bed.

@en