To fulfill the high-temperature application requirement of high-power electronics packaging, Cu nanoparticle sintering technology, with benefits in low-temperature processing and high-melting point, has attracted considerable attention as a promising candidate for the die-attach interconnect. Comprehensive mechanical characterization of the sintered layer at a microscale is necessary to deepen the understanding of the fracture behavior and improve the reliable design of materials. In this study, microscale cantilevers with different notch depths were fabricated in a 20 MPa sintered interconnect layer. Continuous dynamical fracture testing of the microcantilevers was conducted in situ in a scanning electron microscope to detail the failure characteristic of the porous sintered structure. The microscopic fracture toughness of different notched specimens was obtained from the J-integral in the frame of elastic-plastic fracture mechanics. Specimens with deeper notches presented higher resistance to crack extension, while geometry factors of notch-to-width ratio between 0.20 and 0.37 exhibited a relatively stable microscopic fracture toughness ranging from 3.2 ± 0.3 to 3.6 ± 0.1 MPa m^1/2.