State-of-the-art triple cation, mixed halide perovskites are extensively studied in perovskite solar cells, showing very promising performance and stability. However, an in-depth fundamental understanding of how the phase behavior in Cs_0.05FA_0.85MA_0.10Pb(I_0.97Br_0.03)₃ (CsMAFA) affects the optoelectronic properties is still lacking. The refined unit cell parameters a and c in combination with the thermal expansion coefficients derived from X-ray diffraction patterns reveal that CsMAFA undergoes an α–β phase transition at ≈280 K and another transition to the γ-phase at ≈180 K. From the analyses of the electrodeless microwave photoconductivity measurements it is shown that shallow traps only in the γ-phase negatively affect the charge carrier dynamics. Most importantly, CsMAFA exhibits the lowest amount of microstrain in the β-phase at around 240 K, corresponding to the lowest amount of trap density, which translates into the longest charge carrier diffusion length for electrons and holes. Below 200 K a considerable increase in deep trap states is found most likely related to the temperature-induced compressive microstrain leading to a huge imbalance in charge carrier diffusion lengths between electrons and holes. This work provides valuable insight into how temperature-dependent changes in structure affect the charge carrier dynamics in FA-rich perovskites.

Solution-processed quasi-2D perovskites are promising for stable and efficient solar cells because of their superior environmental stability compared to 3D perovskites and tunable optoelectronic properties. Changing the number of inorganic layers (n) sandwiched between the organic spacers allows for tuning of the bandgap. However, narrowing the phase distribution around a specific n-value is a challenge. In-situ UV–vis–NIR absorption spectroscopy is used to time-resolve the crystallization dynamics of quasi-2D butylammonium-based (BA) perovskites with <n> = 4, processed from N,N-dimethylformamide (DMF) in the presence of different co-solvents. By combining with photoluminescence, transient absorption, and grazing-incidence wide-angle X-ray scattering, the crystallization is correlated to the distribution of phases with different n-values. Infrared spectroscopy and density functional theory reveal that the phase distribution correlates with perovskite precursor—co-solvent interaction energies and that stronger interactions shift the phase distribution towards smaller n-values. Careful tuning of the solvent/co-solvent ratio provides a more homogeneous phase distribution, with highly oriented perovskite crystals and suppressed formation of n = 1–2 phases, providing a power conversion efficiency for BA₂MA₃Pb₄I₁₃ solar cells that increases from 3.5% when processed from DMF to over 11% and 10% when processed from DMF/dimethyl sulfoxide and DMF/N-methyl-2-pyrrolidone mixtures, respectively.