The influence of outward extracellular electron transfer (EET) of Pseudomonas aeruginosa in accelerating corrosion of 304 stainless steel was investigated. With less NO₃⁻ available as electron acceptor, P. aeruginosa biofilm accelerated the pitting corrosion. The ICP-MS and XPS results indicated that P. aeruginosa promoted the bioreductive dissolution of iron oxides in the passive film of stainless steel. Using in situ scanning electrochemical microscopy, we established a relationship between this accelerated deterioration of the passive film and the EET process mediated by the conversion of the redox states of pyocyanin secreted by P. aeruginosa.

This work introduces a novel nanocomposite coating with dual-action self-healing corrosion protection activated by the photothermal response of plasmonic titanium nitride nanoparticles (TiN NPs). TiN@mesoporous SiO₂ core–shell nanocontainers were developed as reservoirs for benzotriazole (BTA) corrosion inhibitors and incorporated into the shape memory epoxy coating matrix. Under near-infrared (NIR) light irradiation, the thermogenesis effect of TiN could not only promote the release of corrosion inhibitors from nanocontainers into the crevice, but also trigger the shape memory effect of damaged epoxy to merge the coating scratch. As such, the dual-action self-healing mechanisms combining the formation of an inhibitor-based protective layer and the scratch closure efficiently suppressed the corrosion process at the exposed metal surface. Surface characterization and electrochemical measurement results proved that the nanocomposite coating incorporated with 2 wt% of TiN-BTA@SiO₂ exhibited the optimal corrosion protection as well as an excellent self-healing performance that can be initiated within 30 s of NIR illumination. This photo-controlled self-healing approach is potentially useful in designing next-generation self-healing coatings with ultrafast response time and high healing efficiency.

In this study, a new self-healing shape memory polymer (SMP) coating was prepared to protect the aluminum alloy 2024-T3 from corrosion by the incorporation of dual-function microspheres containing polycaprolactone and the corrosion inhibitor 8-hydroxyquinoline (8HQ). The self-healing properties of the coatings were investigated via scanning electron microscopy, electrochemical impedance spectroscopy, and scanning electrochemical microscopy following the application of different healing conditions. The results demonstrated that the coating possessed a triple-Action self-healing ability enabled by the cooperation of the 8HQ inhibitor, the SMP coating matrix, and the melted microspheres. The coating released 8HQ in a pH-dependent fashion and immediately suppressed corrosion within the coating scratch. After heat treatment, the scratched coating exhibited excellent recovery of its anticorrosion performance, which was attributed to the simultaneous initiation of scratch closure by the shape memory effect of the coating matrix, sealing of the scratch by the melted microspheres, and the synergistic effect of corrosion inhibition by 8HQ.

This work introduces a new self-healing superhydrophobic coating based on dual actions by the corrosion inhibitor benzotriazole (BTA) and an epoxy-based shape memory polymer (SMP). Damage to the surface morphology (e.g., crushed areas and scratches) and the corresponding superhydrophobicity are shown to be rapidly healed through a simple heat treatment at 60 °C for 20 min. Electrochemical impedance spectroscopy (EIS) and scanning electrochemical microscopy (SECM) were used to study the anti-corrosion performance of the scratched and the healed superhydrophobic coatings immersed in a 3.5 wt% NaCl solution. The results revealed that the anti-corrosion performance of the scratched coatings was improved upon the incorporation of BTA. After the heat treatment, the scratched superhydrophobic coatings exhibited excellent recovery of their anti-corrosion performance, which is attributed to the closure of the scratch by the shape memory effect and to the improved inhibition efficiency of BTA. Furthermore, we found that the pre-existing corrosion product inside the coating scratch could hinder the scratch closure by the shape memory effect and reduce the coating adhesion in the scratched region. However, the addition of BTA effectively suppressed the formation of corrosion products and enhanced the self-healing and adhesion performance under these conditions. Importantly, we also demonstrated that these coatings can be autonomously healed within 1 h in an outdoor environment using sunlight as the heat source.