Microbially influenced corrosion (MIC) of metals exerts a negative effect on the marine environment and causes a great loss of marine facilities. Corrosion prevention in an eco-friendly and sustainable way is a difficult problem to address, especially in the marine environment. In this work, Nocardiopsis dassonville, a corrosive bacteria isolated from the South China Sea was studied by using carbon steel. The results indicate that N. dassonville caused a corrosion loss of 7.68 mg cm⁻² and a corrosion pit of 13.0 μm on the carbon steel surface, but the corrosion is inhibited in the presence of Vibrio sp. EF187016 in the medium. Vibrio sp. EF187016 preferentially occupied the carbon steel surface, forming a protective biofilm that hindered the attachment of N. dassonville. In addition, extracellular polymeric substances extracted from Vibrio sp. EF187016 was added to N. dassonvillei inoculated medium and showed a significant inhibition of MIC on carbon steel.

@en

The influence of dissolved oxygen (DO) and Shewanella algae on the corrosion behavior of pure titanium were systematically studied in this work. The formation of S. algae biofilms on titanium surface was facilitated by the anaerobic environment, which accelerated titanium corrosion. Upon the breakdown of passive film, S. algae acquired electrons from the titanium base substrate through extracellular electron transfer (EET) processes. Various EET-related genes were overexpressed by the low DO condition, leading to enhanced EET kinetics. High concentration DO increased TiO2 content and the thickness of passive film, which enhanced the protective effect and mitigated microbiologically influenced corrosion.@en

Shewanella oneidensis MR-1 is an attractive model microbe for elucidating the biofilm-metal interactions that contribute to the billions of dollars in corrosion damage to industrial applications each year. Multiple mechanisms for S. oneidensis-enhanced corrosion have been proposed, but none of these mechanisms have previously been rigorously investigated with methods that rule out alternative routes for electron transfer. We found that S. oneidensis grown under aerobic conditions formed thick biofilms (∼50 µm) on stainless steel coupons, accelerating corrosion over sterile controls. H₂ and flavins were ruled out as intermediary electron carriers because stainless steel did not reduce riboflavin and previous studies have demonstrated stainless does not generate H₂. Strain ∆mtrCBA, in which the genes for the most abundant porin-cytochrome conduit in S. oneidensis were deleted, corroded stainless steel substantially less than wild-type in aerobic cultures. Wild-type biofilms readily reduced nitrate with stainless steel as the sole electron donor under anaerobic conditions, but strain ∆mtrCBA did not. These results demonstrate that S. oneidensis can directly consume electrons from iron-containing metals and illustrate how direct metal-to-microbe electron transfer can be an important route for corrosion, even in aerobic environments.

@en

Microbiologically influenced corrosion of metals is prevalent in both natural and industrial environments, causing enormous structural damage and economic loss. Exactly how microbes influence corrosion remains controversial. Here, we show that the pitting corrosion of stainless steel is accelerated in the presence of Shewanella oneidensis MR-1 biofilm by extracellular electron transfer between the bacterial cells and the steel electrode, mediated by a riboflavin electron shuttle. From pitting measurements, X-ray photoelectron spectroscopy and Mott-Schottky analyses, the addition of an increased amount of riboflavin is found to induce a more defective passive film on the stainless steel. Electrochemical impedance spectroscopy reveals that enhanced bioanodic and biocathodic process can both promote the corrosion of the stainless steel. Using in situ scanning electrochemical microscopy, we observe that extracellular electron transfer between the bacterium and the stainless steel is bidirectional in nature and switchable depending on the passive or active state of the steel surface.

@en

This work introduces a new self-healing superhydrophobic coating based on dual actions by the corrosion inhibitor benzotriazole (BTA) and an epoxy-based shape memory polymer (SMP). Damage to the surface morphology (e.g., crushed areas and scratches) and the corresponding superhydrophobicity are shown to be rapidly healed through a simple heat treatment at 60 °C for 20 min. Electrochemical impedance spectroscopy (EIS) and scanning electrochemical microscopy (SECM) were used to study the anti-corrosion performance of the scratched and the healed superhydrophobic coatings immersed in a 3.5 wt% NaCl solution. The results revealed that the anti-corrosion performance of the scratched coatings was improved upon the incorporation of BTA. After the heat treatment, the scratched superhydrophobic coatings exhibited excellent recovery of their anti-corrosion performance, which is attributed to the closure of the scratch by the shape memory effect and to the improved inhibition efficiency of BTA. Furthermore, we found that the pre-existing corrosion product inside the coating scratch could hinder the scratch closure by the shape memory effect and reduce the coating adhesion in the scratched region. However, the addition of BTA effectively suppressed the formation of corrosion products and enhanced the self-healing and adhesion performance under these conditions. Importantly, we also demonstrated that these coatings can be autonomously healed within 1 h in an outdoor environment using sunlight as the heat source.

@en