Organic coatings are one of the most used and versatile technologies to mitigate corrosion of metals. However, organic coatings are susceptible to defects and damages that may not be easily detected. If not repaired timely, these defects may develop into major coating failures due to corrosion occurring in the damaged region, thereby limiting the lifetime of the to be protected structure. Thus, the development of smart coatings that can accurately identify corrosion location and reliably recover the damage autonomously is of particular interest. Herein, we reported a robust, corrosion-sensing and self-healing coating which incorporated pH-sensitive ZIF-8-capped CaCO₃ microcontainers containing the healing agent tung oil (TO) and the corrosion indicator/inhibitor 1,10-phenanthrolin-5-amine (APhen). The spontaneous leakage of incorporated TO and APhen was restrained, and the release initiated when local pH variation occurred. The corrosion protection performance of the coatings implanted with different contents of smart microcontainers were evaluated. The intact epoxy coating containing 7.5 wt% of the microcontainers exhibited the best protection performance with low water absorption (0.65 wt%), low O₂ permeability (0.21 × 10^–15 cm³ cm cm⁻² s⁻¹ Pa⁻¹), and a high storage modulus (3.0 GPa). Electrochemical impedance spectroscopy (EIS) measurements in 3.5 wt% NaCl solution demonstrated superior durability of the composite coating after self-healing. The immersion test and neutral salt spray test confirmed the coating can accurately report corrosion sites via coloration.

In this work, an active protective epoxy coating with weathering resistant, corrosion-warning, and self-healing properties was developed by incorporating tannic acid (TA) loaded mesoporous silica (MSN-TA) nanocontainers. The introduction of MSN-TA nanocontainers could alleviate the coating degradation via scavenging the radicals generated during UV irradiation. Compared with the blank coating, the coating containing 5 wt.% MSN-TA nanocontainers exhibited much less degradation in surface morphology, wettability and glossiness, and maintained a good barrier property after 384 h of accelerated weathering. Once the coating was damaged, the released TA could react with the Fe³⁺ ions to form a chelate that endowed the coating scratch with a visible black coloration, i.e. triggering a self-warning capability to indicate the initial onset of corrosion. In addition, the generated chelate could inhibit extensive corrosion propagation, offering a significant self-healing effect demonstrated by the stabilized impedance modulus values during 28 days of immersion in NaCl solution.

This work introduces a novel nanocomposite coating with dual-action self-healing corrosion protection activated by the photothermal response of plasmonic titanium nitride nanoparticles (TiN NPs). TiN@mesoporous SiO₂ core–shell nanocontainers were developed as reservoirs for benzotriazole (BTA) corrosion inhibitors and incorporated into the shape memory epoxy coating matrix. Under near-infrared (NIR) light irradiation, the thermogenesis effect of TiN could not only promote the release of corrosion inhibitors from nanocontainers into the crevice, but also trigger the shape memory effect of damaged epoxy to merge the coating scratch. As such, the dual-action self-healing mechanisms combining the formation of an inhibitor-based protective layer and the scratch closure efficiently suppressed the corrosion process at the exposed metal surface. Surface characterization and electrochemical measurement results proved that the nanocomposite coating incorporated with 2 wt% of TiN-BTA@SiO₂ exhibited the optimal corrosion protection as well as an excellent self-healing performance that can be initiated within 30 s of NIR illumination. This photo-controlled self-healing approach is potentially useful in designing next-generation self-healing coatings with ultrafast response time and high healing efficiency.