This paper presents an experimental investigation on the short-term creep recovery of cement paste at micrometre length scale. Micro-cantilever beams were fabricated and tested with 8 different loading series using the nanoindenter. It is found that cement pastes show high recovery ratios (>80%) even subjected to very high stress levels. Relatively lower recovery ratios and non-linear creep were also observed for w/c 0.4 samples under high stress levels. A good agreement is found between the results predicted using the linear superposition principle and the experimental results except for the measured non-linear creep in w/c 0.4 samples. It is suggested that the short-term creep recovery may be associated with the microscale stress redistribution or the reversible internal water movement. The observed non-linear creep under the highest stress level may be due to the higher density of microcracks generated during the loading stage, which may further promote the water transfer.

This study proposes an experimental method for studying the short-term creep behaviour of cement paste at micro-scale. The micro-bending tests on miniaturized cantilever beams were used to characterize the viscoelastic properties of cement paste. The effects of w/b ratio, the type of binder and the stress level on the microscopic creep behaviour were investigated. It is found that the short-term creep of cement paste at microscale can be satisfactorily described by a power-law function. A linear viscoelastic behaviour has been observed in different cementitious systems at the microscale with the stress level up to 67.9%. When compared with the creep results in microindentation tests and conventional macroscopic tests, the obtained creep compliance function in this study is found to be both qualitatively and quantitatively representative of the macroscopic results. This experimental study underlines the importance of microstructural effect on the creep behaviours of cementitious materials at microscale.