The giant magnetocaloric effect is widely achieved in hexagonal MnMX-based (M = Co or Ni, X = Si or Ge) ferromagnets at their first-order magnetostructural transition. However, the thermal hysteresis and low sensitivity of the magnetostructural transition to the magnetic field inevitably lead to a sizeable irreversibility of the low-field magnetocaloric effect. Here, we show an alternative way to realize a reversible low-field magnetocaloric effect in MnMX-based alloys by taking advantage of the second-order phase transition. With introducing Cu into Co in stoichiometric MnCoGe alloy, the martensitic transition is stabilized at high temperature, while the Curie temperature of the orthorhombic phase is reduced to room temperature. As a result, a second-order magnetic transition with a negligible thermal hysteresis and a large magnetization change can be observed, enabling a reversible magnetocaloric effect. By both calorimetric and direct measurements, a reversible adiabatic temperature change of about 1 K is obtained under a field change of 0-1 T at 304 K, which is larger than that obtained in a first-order magnetostructural transition. To gain a better insight into the origin of these experimental results, first-principles calculations are carried out to characterize the chemical bonds and the magnetic exchange interaction. Our work provides an understanding of the MnCoGe alloy and indicates a feasible route to improve the reversibility of the low-field magnetocaloric effect in the MnMX system.

The first-order magneto-elastic transition in the Mn–Fe–P–Si alloys can be tailored by vanadium substitution. Alloys with a suitable V substitution provide an excellent magnetocaloric effect with minor hysteresis in low magnetic fields up to 1.2 T. Mössbauer measurements show that the hyperfine field is reduced by V substitution. Neutron diffraction reveals that Fe is substituted by V on the 3f site and the magnetic moment on the 3f site is enhanced by the V substitution. The modified magnetic exchange field around the 3f and 3g positions in the lattice can be utilized to design suitable magnetocaloric materials that operate in low magnetic fields.

A rotary active magnetic regeneration refrigerator prototype named FAME Cooler was developed for studying the performance of different magnetocaloric materials in a realistic practical environment. The rotary magnetic field source generates an average magnetic field of 0.875 T within a volume of 0.71 l The regenerator is designed asymmetrically and holds in total 1.18 kg of gadolinium spheres for a first performance test. Combined with a real-time controlled programmable solenoid-valves system, different working parameters or thermodynamic cycles can be applied. In the performance test, while the temperature of system hot side was fixed at 295 K, under a utilization condition of 0.25, this prototype achieved a maximum zero-span cooling power of 162.4 W, and a zero-power temperature span of 11.6 K. Under a utilization condition of 0.15, a maximum COP of 1.85 was reached. These performance metrics are comparable with existing magnetic heat pump devices of the same scale.