This study characterized the morphology, high-temperature property, rheological property, adhesion, cohesion, and chemical component of asphalt binder under aqueous solutions of different pH values. Then the physicochemical properties of asphalt binder were comprehensively evaluated by the improved radar chart. The properties of asphalt binder stripped layer-by-layer were explored to elucidate its gradient damage behaviors. The results indicate that the pH 3 solution reveals the greatest impact on the morphology of 90 asphalt (90 A) and styrene-butadiene-styrene modified asphalt (SBS MA), leading to the wide cracks on 90 A and the network cracks on SBS MA. The comprehensive assessment index of 90 A exposed to pH 3, pH 5, pH 7, pH 9, and pH 11 solutions can be reduced by 20.8%, 20.2%, 1.5%, 14.0%, and 25.5%, respectively. While for SBS MA, its corresponding values variation are 23.2%, 17.7%, 4.6%, 8.7%, and 13.0%, respectively. The acid solutions significantly affect the comprehensive properties of 90 A, but their pH value has little effect. 90 A exposure to the higher pH value of alkali solution reveals the worse comprehensive properties. Acid solute and alkali solute can aggravate the effect of aqueous solution on the comprehensive properties of SBS MA, and the degree of aggravation increases with the increase of solute concentration. The properties of asphalt binders exhibit varied gradient damage behaviors under different solute environments. The most serious damage occurs at 25–50 µm of 90 A and 0–50 µm of SBS MA. This study facilitates an accurate understanding of the mechanism of pavement distresses and composition design and construction utilization of asphalt binders.

Self-healing is a biological phenomenon in which living organism responds to the suffered damage in a complex way. Inspired by the self-healing phenomenon in nature, various biomimetic healing methods rooted in intrinsic or extrinsic healing mechanisms have been explored. Research on novel self-healing asphalt materials with intelligent response is at the cutting-edge of materials science and offers a potential strategy for building long-life and low-carbon asphalt concrete infrastructure. This paper describes the progress of research on extrinsic self-healing asphalt materials and makes a clear distinction between intrinsic and extrinsic self-healing. The asphalt self-healing mechanism is interpreted by capillary flow theory, phase field theory, molecular diffusion theory and surface energy theory form various perspective. The extrinsic self-healing strategies including thermal induced healing and rejuvenator induced healing are proposed to enhance the healing level of cracked asphalt materials. A brief review of the methods including fracture-healing test and fatigue-healing test for assessing the efficacy of different extrinsic healing methods is presented. The thermal induced healing method bring high crack repair efficiency for asphalt concrete and the rejuvenator induced healing strategy not only improve the healing ratio of cracked asphalt concrete but also regenerate the ageing asphalt in situ. Important lessons for prospective research on the creation of novel self-healing asphalt materials are highlighted.

Polymer Ca-alginate capsules with rejuvenator bring a high healing level for asphalt concrete under dry healing environments; however, the healing levels of bituminous mixtures containing capsules under water healing conditions are still unknown. In view of this, this study aimed at exploring the healing levels of asphalt concrete containing polymer capsules under various solution healing conditions following cyclic loads. This study involved the preparation of capsules, followed by the evaluation of their morphological characteristics, resilience to compression, thermal endurance, and rejuvenator content. The assessment of the healing properties of asphalt concrete utilizing capsules was conducted through a fracture–heal–refracture examination. This study conducted Fourier transform infrared spectrum experiments to determine the rejuvenator release ratio of capsules under dry conditions and the remaining rejuvenator content in extracted bituminous binder from capsule–asphalt concrete after solution treatment. Meanwhile, a dynamic shear rheometer was utilized to investigate the rheological characteristics of asphalt binder. Results revealed that the healing ratios of capsule–asphalt concrete beams under a dry healing environment were significantly higher than that of beams under various solution healing conditions, and the alkali solution has the worst effect on the improvement in healing ratio. The coupled impact of moisture intrusion and ion erosion resulted in an enhancement of complex modulus of asphalt binder while concurrently reducing its phase angle. Consequently, the restorative capacity of the asphalt binder was weakened.

Moisture erosion is one of the key factors leading to asphalt pavement damage, and the erosion depth indicates the moisture damage level but it is usually neglected. In order to study the moisture erosion and the erosion depth, this study characterized the chemical structure, rheological property and adhesion property of asphalt at different depths after immersion for different periods. To further explore the diffusion mechanism of eroded asphalt, a Log-log numerical model was established based on the Fick's second law to calculate the diffusion coefficient throughout the depth. The results indicate that it takes just four hours for water to penetrate a 25 μm asphalt film. The relation between erosion depth and immersion period presents three stages, and the process can be fitted with a polynomial model. At the macroscopic level, there is a lag between the changes in adhesion property with chemical structure and rheological property. Additionally, the periodicity of moisture erosion process was verified by the calculation of diffusion factor. In summary, the diffusion mechanism of eroded asphalt by moisture can provide a theoretical basis for the development of laboratory moisture erosion test specification, thus avoiding the waste of raw materials.