Metal halide perovskite solar cells (PSCs) are of interest for high altitude and space applications due to their lightweight and versatile form factor. However, their resilience toward the particle spectrum encountered in space is still of concern. For space cells, the effect of these particles is condensed into an equivalent 1 MeV electron fluence. The effect of high doses of 1 MeV e-beam radiation up to an accumulated fluence to 10¹⁶ e⁻ cm⁻² on methylammonium lead iodide perovskite thin films and solar cells is probed. By using substrate and encapsulation materials that are stable under the high energy e-beam radiation, its net effect on the perovskite film and solar cells can be studied. The quartz substrate-based PSCs are stable under the high doses of 1 MeV e-beam irradiation. Time-resolved microwave conductivity analysis on pristine and irradiated films indicates that there is a small reduction in the charge carrier diffusion length upon irradiation. Nevertheless, this diffusion length remains larger than the perovskite film thickness used in the solar cells, even for the highest accumulated fluence of 10¹⁶ e⁻ cm⁻². This demonstrates that PSCs are promising candidates for space applications.

@en

Abstract

The addition of Sr2+ in CH3NH3PbI3 perovskite films enhances the charge carrier collection efficiency of solar cells leading to very high fill factors, up to 85%. The charge carrier lifetime of Sr2+-containing perovskites is in excess of 40 μs, longer than those reported for perovskite single crystals.
@en