Compared with traditional techniques, solid-state magnetocaloric phase transition materials (MPTMs), based on the giant magnetocaloric effect (GMCE), can achieve a higher energy conversion efficiency for caloric applications. As one of the most promising MPTMs, the hexagonal (Mn,Fe)₂(P,Si)-based compounds host some advantages, but the existing hysteresis and relatively unstable GMCE properties need to be properly tackled. In this study, it is found that substitutions with Ni, Pd, and Pt can maintain and even enhance the GMCE (≈8.7% maximum improvement of |Δs_m|). For a magnetic field change of Δμ₀H = 2 T, all samples obtain a |Δs_m| in the range of 20–25 J kg⁻¹ K⁻¹ with a low thermal hysteresis ΔT_hys (≤5.6 K). The performance surpasses almost all other (Mn,Fe)₂(P,Si)-based materials with ΔT_hys (<10 K) reported until now. The occupancy of substitutional Ni/Pd/Pt atoms is determined by X-ray diffraction, neutron diffraction, and density functional theory calculations. The difference in GMCE properties upon doping is understood from the competition between a weakening of the magnetic exchange interactions and the different degrees of orbital hybridization among 3d-4d-5d elements. The studies elaborate on the responsible mechanism and provide a general strategy through d-block doping to further optimize the GMCE of this materials family.

@en

The influence of doping with the 5d transition metal W has been studied in the quaternary (Mn,Fe)₂(P,Si) based giant magnetocaloric compounds, which is one of the most promising systems for magnetic refrigeration. It is found that W substitution can separately decrease the Curie temperature T_C and retain the thermal hysteresis ∆T_hys at an almost constant level (∼5 K) for Mn_0.6Fe_1.27-xW_xP_0.64Si_0.36 (x ≤ 0.02). Low-content W doping conserves the good magnetocaloric effect (MCE) without an obvious degradation. For x ≤ 0.02 the average magnetic entropy change |∆S_m| amounts to 11.4 Jkg⁻¹K⁻¹ for an applied magnetic field change of 2 T and the adiabatic temperature change ∆T_ad amounts to 3.9 K for an applied magnetic field change of 1.5 T. The occupancy of substitutional W atoms is determined by XRD experiments and DFT calculations. Our studies provide a good strategy to further optimize the MCE of this material family.

@en

The growing demand for energy highlights the need for developing more efficient and environmentally friendly technologies. Magnetic cooling based on the magnetocaloric effect is a promising alternative for compressor-based refrigeration. Among various magnetocaloric materials, Mn-based alloys appear especially attractive due to their low cost, high abundance and the potentially large magnetic moment density. We aimed to obtain a large magnetocaloric effect at room temperature in various non-toxic and inexpensive magnetocaloric materials. Thus, this thesis contains the study on the magnetism, magnetocaloric effect and (micro)structure of three families of Mn-based magnetocaloric materials: (Mn,Fe)2(P,Si), Mn3Sn1-xAxC antiperovskite carbides, MnNiSi half Heusler alloys. A particular part of this dissertation focuses on the elucidation of magnetic structures in antiperovskite carbides.@en

Structural, magnetic and magnetocaloric properties of Mn₃Sn_1-xZn_xC antiperovskite carbides have been studied. With increasing Zn content the first-order magnetic transition (FOMT) is weakened. The Curie temperature (T_C) reduces first from 273 to 197 K and when x > 0.3, T_C increases, reaching its maximum of 430 K for x = 1.0. An increase in T_C is accompanied by pronounced changes in magnetic behaviour and a significant rise in magnetization from 21.82(4) to 76.2(2) Am²kg⁻¹ for x = 0.8 in the maximum applied magnetic field of 5 T. Neutron powder diffraction (NPD) was employed to study the magnetic structure of Mn₃Sn_1-xZn_xC compounds. The refinement of the NPD data for x = 0.3 revealed a magnetic structure with propagation vector k = (½,½,0) with a decrease in the canted antiferromagnetic (AFM) moment, which results in a reduction of the negative volume change at the magnetic transition and a decrease in the magnetocaloric effect (MCE). For x = 0.4, the magnetic structure is described by a propagation vector k = (½,½,½) for the AFM moment which dominates at low temperature, with the presence of a minor ferromagnetic (FM) component with a k = (0, 0, 0) propagation vector, which confirms the presence of the ferrimagnetic (FiM) state. For a higher Zn content (x = 0.6), the magnetic moment originates mainly from the FM component found on three independent Mn positions and an additional AFM moment oriented in the a-b plane. The results presented confirm the presence of competing AFM-FM interactions in Mn₃Sn_1-xZn_xC antiperovskite carbides.

@en

The effect of the heat treatment on the magnetism, magnetocaloric effect and microstructure formation has been systematically studied in Fe-rich (Mn,Fe)_y(P,Si) melt-spun ribbons (1.80 ≤ y ≤ 2.00). XRD, SEM and EDS measurements demonstrate that a metal deficiency prompts the stable (Mn,Fe)Si phase, whereas in the metal-rich region the (Mn,Fe)₃Si phase is formed. It is found that the annealing temperature influences the composition and lattice parameters of the (Mn,Fe)_y(P,Si) alloys, which greatly affects the Curie temperature (T_C). For the optimal metal/non-metal ratio y the magnetic entropy change (|ΔS_m|) is found to increase from 5.5 to 15.0 Jkg⁻¹K⁻¹ in a magnetic field change of 2 T by varying the annealing temperature from 1313 to 1433 K, indicating an enhancement of the first-order magnetic transition (FOMT). The presented results reveal that the secondary phase and magnetic properties in the (Mn,Fe)_y(P,Si) system can be tuned by varying the annealing temperature and by adjusting the metal/non-metal ratio y.

@en

The effect of Co and Ni doping on the structure, magnetic and magnetocaloric properties of Fe-rich (Mn,Fe)₂(P,Si) compounds was studied. With increasing Co and Ni content, both the Curie temperature (T_c) and the thermal hysteresis (ΔT_hys) decreased, whereas the hexagonal P-62 m crystal structure was maintained. A pronounced reduction in hysteresis was observed upon Co doping, while a significant reduction in Curie temperature was found upon Ni doping. Mössbauer spectroscopy measurements and DFT calculations indicated the substitution of Fe at the 3f site for both Co and Ni doping. Rietveld refinement of the X-ray diffraction data showed that Co substitute atoms in the main phase and the impurity phase, while Ni exhibits an affinity to the main phase. Magnetization measurements on the Co doped samples revealed an increase in magnetization for 2 at.% of Co, followed by a decrease for higher concentrations. DFT calculations showed that the magnetic moment on the 3f site is enhanced by Co substitution, whereas an opposite trend was observed for Ni substitution.

@en

The novel all-d-metal Ni(Co)MnTi based magnetic Heusler alloys provide an adjustable giant magnetocaloric effect and good mechanical properties. We report that the second-order magnetic phase transition can be tailored in this all-d-metal NiCoMnTi based Heusler system by optimizing the Mn/Ti ratio, resulting in a reversible ferromagnetic-to-paramagnetic magnetic transition. A candidate material Ni₃₃Co₁₇Mn₃₀Ti₂₀ with a magnetic entropy change ∆S_m of 2.3 Jkg⁻¹K⁻¹ for a magnetic field change of 0–5 T, has been identified. The T_C and saturation magnetization M_S can be controlled by adjusting the Ni/Co concentration and doping non-magnetic Cu atoms. The compositional maps of T_C and M_S have been established. Density functional theory (DFT) calculations reveal a direct correlation between the magnetic moments and the Co content. By combining XRD, SQUID, SEM and DFT calculations, the (micro)structural and magnetocaloric properties have been investigated systematically. This study provides a detailed insight in the magnetic phase transition for this all-d-metal Ni(Co)MnTi-based Heusler alloy system.