A hybrid tandem solar cell consisting of a thin-film, nanocrystalline silicon top junction and a siliconheterojunction bottom junction is proposed as a supporting solar cell for photoelectrochemical applications.Tunneling recombination junction engineering is shown to be an important consideration indesigning this type of solar cell. The best hybrid cell produced has a spectral utilization of 30.6 mA cm2a JSC of 14 mA cm2, a VOC of 1.1 V, a fill factor of 0.67 and thus an efficiency of 10.3%. A high solar-tohydrogenefficiency of 7.9% can be predicted when using the hybrid cell in conjunction with current a-SiCphotocathode technology.@en

Atomic layer deposition (ALD) was used to deposit nanoparticles and thin films of Pt onto etched p-type Si(111) wafers and glassy carbon discs. Using precursors of MeCpPtMe3 and ozone and a temperature window of 200-300 °C, the growth rate was 80-110 pm/cycle. X-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM), and scanning electron microscopy (SEM) were used to analyze the composition, structure, morphology, and thickness of the ALD-grown Pt nanoparticle films. The catalytic activity of the ALD-grown Pt for the hydrogen evolution reaction was shown to be equivalent to that of e-beam evaporated Pt on glassy carbon electrode.@en