Silicon integrated circuits (ICs) are central to the next-generation miniature active neural implants, whether packaged in soft polymers for flexible bioelectronics or implanted as bare die for neural probes. These emerging applications bring the IC closer to the corrosive body environment, raising reliability concerns, particularly for chronic use. Here, we evaluate the inherent hermeticity of bare die ICs, and examine the potential of polydimethylsiloxane (PDMS), a moisture-permeable elastomer, as a standalone encapsulation material. For this aim, the electrical and material performance of ICs sourced from two foundries was evaluated through one-year accelerated in vitro and in vivo studies. ICs featured custom-designed test structures and were partially PDMS coated, creating two regions on each chip, uncoated “bare die” and “PDMS-coated”. During the accelerated in vitro study, ICs were electrically biased and periodically monitored. Results revealed stable electrical performance, indicating the unaffected operation of ICs even when directly exposed to physiological fluids. Despite this, material analysis revealed IC degradation in the bare regions. PDMS-coated regions, however, revealed limited degradation, making PDMS a suitable IC encapsulant for years-long implantation. Based on the new insights, guidelines are proposed that may enhance the longevity of implantable ICs, broadening their applications in the biomedical field.@en

In this paper, we investigate the long-term adhesion strength and barrier property of our recently proposed encapsulation stack that includes PDMS-Parylene C and PECVD interlayers (SiO2 and SiC) for adhesion improvement. To evaluate the adhesion strength of our proposed stack, the sample preparation consisted in depositing approximately 25 nm of SiC and 25 nm of SiO2 on half wafers, previously coated with Parylene C. Next, $50 \mu \mathrm{m}$ PDMS was spin-coated on top. Finally, the samples were detached from the Si wafer and soaked in a PBS solution at 67°C to accelerate the aging process. Two samples were also implanted, subcutaneously, on the left and right subscapular regions of a rat. The optical inspection and peel tests performed after two months confirmed our preliminary findings and showed a significant improvement of the adhesion in our proposed encapsulation stack compared to the case of PDMS on Parylene C alone. In addition, the X-ray photoelectron spectroscopy(XPS) analysis at the interface between SiC and Parylene C showed different peaks for the interface compared to the reference spectra, which could be an indication of a chemical bond. Finally, water vapor transmission rate (WVTR) tests were performed to investigate the barrier property of our proposed encapsulation stack against water vapor transmission. The results demonstrated that the proposed stack acts as a significantly (two orders of magnitude) higher barrier against moisture compared to only Parylene C and PDMS encapsulation layers. The proposed method yields a fully transparent encapsulation stack over a broad wavelength spectrum that can be used for the conformal encapsulation of flexible devices and thus, making them compatible with techniques such as optical imaging and optogenetics.@en