Degradation of CIGS solar cells due to the migration of alkali-elements

Theelen, M.J.; Barreau, Nicolas; Hans, V.O.; Steijvers, Henk; Vroon, Zeger; Zeman, M.

Degradation of CIGS solar cells due to the migration of alkali-elements

Conference paper (2015)

Authors

M.J. Theelen TNO Solliance

Nicolas Barreau Université de Nantes

V.O. Hans TNO Solliance

Henk Steijvers TNO Solliance

Zeger Vroon TNO Solliance

M. Zeman Electrical Sustainable Energy

Department

Electrical Sustainable Energy

Reliability Potassium Illumination CIGS Solar cell Molybdenum Damp heat Sodium

To reference this document use:

http://resolver.tudelft.nl/uuid:9b78217a-1070-45c3-8e36-98ef8192a841

More Info

expand_more

Published Date

2015-6

Language

English

Reuse Rights

Other than for strictly personal use, it is not permitted to download, forward or distribute the text or part of it, without the consent of the author(s) and/or copyright holder(s), unless the work is under an open content license such as Creative Commons.

Department

Electrical Sustainable Energy

Abstract

Non-encapsulated CIGS solar cells with different contents of sodium (Na) and potassium (K) were simultaneously exposed to damp heat and illumination. The solar cells with higher alkali (Na, K) content exhibited higher initial conversion efficiencies, but degraded severely within 100 hours, while samples with a lower alkali content retained their efficiency longer. The degradation was likely caused by the migration of alkali atoms, leading to shunting of the solar cells and the formation of alkali rich spots.