In the pursuit of introducing bacteria-based self-healing mortar for masonry repair, this study examined the potential of incorporating a poly-lactic acid (PLA) agent—already established in concrete repair—into cement-lime mortars, typical of historical constructions. Testing prisms constructed with varying lime/cement ratios revealed decreased flexural and compressive strength in high-cement-concentration mortars upon the addition of the agent; for mortars with high lime concentration, however, the agent led to an increase in both strengths. Furthermore, the agent's potential to self-repair was confirmed by allowing the remaining portions of tested samples to heal under humid conditions. Irrespective of mortar composition, cracks were resealed thus confirming the aesthetic, and potentially watertightness, restoration.@en

Cracks represent a prevalent form of damage in masonry structures, posing not only aesthetic concerns but also compromising structural durability; therefore, they are undesirable and need to be repaired. The repointing technique is traditionally implemented in this context, especially in historical masonry. However, this method fails to provide a long-term solution, leaving structures vulnerable to future damage. The paper investigates the applicability of a bio-based self-healing mortar to enable autonomous repair of masonry. This innovative mortar, developed to repair concrete structures, was implemented to explore the capacity of couplets to recover their original bond capacity and aesthetic aspect after multiple damaging events. Specimens built with calciumsilicate and clay bricks were subjected to subsequent cracking cycles using a crack-mouth-opening -displacement controlled bond-wrench test. Experimental results showed that self-repair, in terms of bond restoration and aesthetic filling of cracks, occurs even after multiple cracking cycles when the bio-based mortar is used with both types of bricks, optimizing the autogenous healing (intrinsic) of cement-based mortars. The effectiveness varied also according to the types of brick and healing environment used, e.g. under humid conditions (RH ~ 95%), 50% vs 80% of the original capacity was regained in fully separated couplets made respectively with clay and calcium-silicate bricks.@en

The brick-to-mortar bond often represents the weakest link leading to cracking and failure of masonry structures. For this reason, the in-situ characterization of masonry’s flexural bond behaviour (here defined as flexural bond strength and flexural bond fracture energy), is essential for the assessment of existing buildings. Among masonry bond properties, the flexural bond strength is commonly determined on-site, given the minimal invasiveness of the so-called bond wrench test. However, often the reliability of the results is questioned inputting their large variability to the operator. The present study discharges this assumption by comparing the accuracy of various testing set-ups (manually-operated vs computer-controlled set-ups). Additionally, the influence of the specimen’s type (with/without head joints and couplets vs wallet) on the flexural bond strength assessment is studied providing preliminary correlation factors that can be of help for the in-situ measurement on single-wythe masonry. In addition, to obtain a complete description of the bond behaviour, a new test set-up able to determine the post-peak response is presented. Considerations regarding the dissipated bond fracture energy and its relation to the tensile fracture energy are provided with the support of literature data.

@en

Cracks are one of the most common expressions of damage in masonry structures. Aside from aesthetic issues, they can compromise the overall behaviour of the structure; therefore, they are undesirable and need to be repaired. The repointing technique is traditionally implemented in this context, especially in historical masonry. Nevertheless, future damage is not prevented and may arise again, thus requiring renewed repointing interventions. The paper describes a preliminary study conducted at Delft University of Technology to investigate the applicability of the innovative self-healing technology to enable an automatic repair of masonry cracks. A bacteria-based self-healing mortar, developed to repair existing concrete structures, was implemented to explore the capacity of couplets to recover their original strength and aesthetic aspect after multiple damaging events. Specimens built with calcium-silicate and clay bricks were subjected to subsequent cracking cycles using a crack-mouth-opening-displacement controlled bond-wrench test. Experimental results showed that self-repair, in terms of strength restoration and aesthetic filling of cracks, occurs even after multiple cracking cycles when the self-healing mortar is used with both types of bricks, optimizing the autogenous healing of cement-based mortars. In this context, the healing effectiveness tended to decrease as the crack width and the number of cycles increased. The effectiveness varied also according to the types of brick and healing environment used, e.g. under humid conditions (RH ~ 95%), 50% vs 80% of the original capacity was regained in fully separated couplets made respectively with clay and calcium-silicate bricks. This outcome provides the ground to delineate the remaining testing campaign.

@en

Innovative solutions for seismic-retrofitting existing structures are currently required, as often traditional strategies are expensive, non-reversible, highly invasive, and/or fail to address both serviceability and ultimate limit states together. The present paper describes a preliminary experimental campaign performed at TU Delft to investigate an innovative structural glass window for strengthening masonry buildings. To this purpose, a prototype composed of a timber frame, a semi-rigid adhesive, and a 20 mm thick structural glazing layer was designed. The prototype aimed to improve the structure’s behavior against minor but more frequent service vibrations (SLS), as well as against ultimate ones (ULS). Specifically, an increase in the structure’s in-plane capacity and stiffness was targeted to reduce cracking at low drifts/displacements, while at larger drifts, the adhesive’s tearing and timber crushing were used to activate damping. To evaluate the prototype’s performance, a quasi-static, cyclic, in-plane test on a strengthened full-scale wall was performed and compared with available data on a similar, yet unstrengthened, wall. Although the benefits were not pronounced in terms of cracking and energy dissipation, the implementation of the proposed strategy provided an increase in terms of initial stiffness (18%), force capacity (8%, 36%), and ductility (220%, 135%). This outcome provides the ground for numerical studies that will help better delineate the proposed strategy and improve the current design.@en