Gallium nitride (GaN) has attracted increased attention because of superior material properties, such as high electron saturation velocity and high electrical field strength, which are promising for high-power microwave applications. We report on a high-performance vertical GaN-based Schottky barrier diode (SBD) and its demonstration in a microwave power limiter for the first time. The fabricated SBD achieved a very low differential specific on-resistance (R_ON,sp) of 0.21 mΩ·cm², attributed to the steep-mesa technology, which assists in reducing the spacing between the edge of the anode and cathode to 2 µm. Meanwhile, a low leakage current of ~10⁻⁹ A/cm²@−10 V, a high forward current density of 9.4 kA/cm² at 3 V in DC, and an ideality factor of 1.04 were achieved. Scattering parameter measurements showed that the insertion loss (S₂₁ ) was lower than −3 dB until 3 GHz. In addition, a microwave power limiter circuit with two anti-parallel diodes was built and measured on an alumina substrate. The input power level reached 40 dBm (10 watts) in continuous-wave mode at 2 GHz, with a corresponding leakage power of 27.2 dBm (0.5 watts) at the output port of the limiter, exhibiting the great potential of GaN SBD in microwave power limiters.

We report a high-performance GaN Schottky barrier diode (SBD) on a sapphire substrate with a novel post-mesa nitridation technique and its application in a high-power microwave detection circuit. The fabricated SBD achieved a very high forward current density of 9.19 kA cm-2 at 3 V, a low specific on-resistance (RON,sp) of 0.22 mO cm2 and breakdown voltage of 106 V. An extremely high output current of 400 mA was obtained when the detected power reached 38.4 dBm@3 GHz in pulsed-wave mode with a small anode diameter of 70 μm. Meanwhile, broadband detection at frequencies ranging from 1 to 6 GHz was achieved at 33 dBm in continuous-wave mode.