Structural, defect and magnetic properties of the TiO₂:Co films are investigated. We varied the maximum Co⁺-implantation concentration from 0.5 at.% up to 5 at.%. A concentration window, which is considered as a threshold for the formation of metallic secondary phases is found. At this concentration it is also observed that the majority of the dopant atoms are incorporated into the host lattice.