Additive manufacturing has facilitated fabrication of complex and patient-specific metallic meta-biomaterials that offer an unprecedented collection of mechanical, mass transport, and biological properties as well as a fully interconnected porous structure. However, applying meta-biomaterials for addressing unmet clinical needs in orthopedic surgery requires additional surface functionalities that should be induced through tailor-made coatings. Here, we developed multi-functional layer-by-layer coatings to simultaneously prevent implant-associated infections and stimulate bone tissue regeneration. We applied multiple layers of gelatin- and chitosan-based coatings containing either bone morphogenetic protein (BMP)-2 or vancomycin on the surface of selective laser melted porous structures made from commercial pure Titanium (CP Ti) and designed using a triply periodic minimal surface (i.e., sheet gyroid). The additive manufacturing process resulted in a porous structure and met the the design values comparatively. X-ray photoelectron spectroscopy spectra confirmed the presence and composition of the coating layers. The release profiles showed a continued release of both vancomycin and BMP-2 for 2–3 weeks. Furthermore, the developed meta-biomaterials exhibited a very strong antibacterial behavior with up to 8 orders of magnitude reduction in both planktonic and implant-adherent bacteria and no signs of biofilm formation. The osteogenic differentiation of mesenchymal stem cells was enhanced, as shown by two-fold increase in the alkaline phosphatase activity and up to four-fold increase in the mineralization of all experimental groups containing BMP-2. Eight-week subcutaneous implantation in vivo showed no signs of a foreign body response, while connective tissue ingrowth was promoted by the layer-by-layer coating. These results unequivocally confirm the superior multi-functional performance of the developed biomaterials.

@en

Enhanced bone tissue regeneration and improved osseointegration are among the most important goals in design of multifunctional orthopedic biomaterials. In this study, we used additive manufacturing (selective laser melting) to develop multifunctional porous nitinol that combines superelasticity with a rationally designed microarchitecture and biofunctionalized surface. The rational design based on triply periodic minimal surfaces aimed to properly adjust the pore size, increase the surface area (thereby amplifying the effects of surface biofunctionalization), and resemble the curvature characteristics of trabecular bone. The surface of additively manufactured (AM) porous nitinol was biofunctionalized using polydopamine-immobilized rhBMP2 for better control of the release kinetics. The actual morphological properties of porous nitinol measured by microcomputed tomography (e.g., open/close porosity, and surface area) closely matched the design values. The superelasticity originated from the austenite phase formed in the nitinol porous structure at room temperature. Polydopamine and rhBMP2 signature peaks were confirmed by X-ray photoelectron spectroscopy and Fourier transform infrared spectroscopy tests. The release of rhBMP2 continued until 28 days. The early time and long-term release profiles were found to be adjustable independent of each other. In vitro cell culture showed improved cell attachment, cell proliferation, cell morphology (spreading, spindle-like shape), and cell coverage as well as elevated levels of ALP activity and increased calcium content for biofunctionalized surfaces as compared to as-manufactured specimens. The demonstrated functionalities of porous nitinol could be used as a basis for deployable orthopedic implants with rationally designed microarchitectures that maximize bone tissue regeneration performance by release of biomolecules with adjustable and well-controlled release profiles.@en