Vitreous cryo-section-induced compression influences the interpretation and the reliability of electron microscopy images and tomographic reconstructions. Previous studies of this deformation have been focused at the cellular level where considerable compression occurs, yet the degree of possible intracellular macromolecular deformation has remained unclear. Here, electron cryo-tomographic reconstructions of vitreous cryo-sections show that SOS ribosomes, both intracellular and in an isolated state, appear able to resist section-induced compression. Our observations indicate that vitreous section-induced compression is non-uniform between whole cells that have been sectioned and their intracellular macromolecular complexes. We conclude that electron cryo-tomography of vitreous cryo-sections, in spite of section-induced compression, is a suitable technique for charting the structural organization of cellular nanomachines, such as ribosomes, in a cellular environment.@en

We studied the formation of locally coated sub-10-nm nanopores fabricated by ion-beam milling and ion-beam-induced deposition (IBID) in a thin silicon nitride membrane. Two typical precursor gases representing conductive ((CH3)(3)Pt(CpCH3). CPC for short) and insulating (tetra ethyl oxysilane, TEOS for short) material deposition are used. Three-dimensional electron tomography, EDX and EELS analysis are used to measure the changes in chemical composition and shape of the pores after their formation and at various stages of pore shrinkage. The formation and shrinkage are shown to be due to a shifting competition between IBID and material sputtering during ion-beam exposure. The chemical distribution at the rim of the nanopore is dependent on the precursor gases used: CPC forms a thin carbon layer with small embedded Pt particles at the top and inner surfaces of the nanopore, whereas TEOS forms SiOxCy with Ga particles dispersed at the rim of the nanopore.@en