The most common methods for detecting chloride-induced corrosion in concrete bridges are half-cell potential (HCP) mapping, electrical resistivity (ER) measurements, and chloride concentration testing, combined with visual inspection and cover measurements. However, studies on corrosion detection in pretensioned structures are rare. To investigate the applicability and accuracy of the above methods for corrosion detection in pretensioned bridge girders, we measured pretensioned I-shaped girders exposed to the Norwegian coastal climate for 33 years. We found that, even combined, the above methods can only reliably identify general areas with various probabilities of corrosion. Despite severe concrete cracking and high chloride content, only small corrosion spots were found in strands. Because HCP cannot distinguish corrosion probability in the closely spaced strands from other electrically connected bars, the actual condition of individual strands can be found only when concrete cover is locally removed. Wet concrete with high chloride content and accordingly low HCP and low ER was found only in or near the girder support zones, which can therefore be considered the areas most susceptible to chloride-induced corrosion. We conclude by proposing a procedure for the inspection and assessment of pretensioned girders in a marine environment.

@en

The steel–concrete interface (SCI) is known to influence corrosion of steel in concrete. However, due to the numerous factors affecting the SCI—including steel properties, concrete properties, execution, and exposure conditions—it remains unclear which factors have the most dominant impact on the susceptibility of reinforced concrete to corrosion. In this literature review, prepared by members of RILEM technical committee 262-SCI, an attempt is made to elucidate the effect of numerous SCI characteristics on chloride-induced corrosion initiation of steel in concrete. We use a method to quantify and normalize the effect of individual SCI characteristics based on different literature results, which allows comparing them in a comprehensive context. It is found that the different SCI characteristics have received highly unbalanced research attention. Parameters such as w/b ratio and cement type have been studied most extensively. Interestingly, however, literature consistently indicates that those parameters have merely a moderate effect on the corrosion susceptibility of steel in concrete. Considerably more pronounced effects were identified for (1) steel properties, including metallurgy, presence of mill scale or rust layers, and surface roughness, and (2) the moisture state. Unfortunately, however, these aspects have received comparatively little research attention. Due to their apparently strong influence, future corrosion studies as well as developments towards predicting corrosion initiation in concrete would benefit from considering those aspects. Particularly the working mechanisms related to the moisture conditions in microscopic and macroscopic voids at the SCI is complex and presents major opportunities for further research in corrosion of steel in concrete.@en

This study was based on findings from the Norwegian Public Roads Administration's Bridge Management System and field investigations on corrosion damage in pretensioned Norwegian standard I-beam (NIB) girders in 227 coastal climate bridges. The main durability design parameters are summarized and related to regulations over the last 80 years. Environmental exposure is discussed in the light of the global, local, and micro climate. We found that 51% of the bridges have girder corrosion damage. The percentage is highest for bridges built when the cover thickness required was lowest. Cover thickness below that required (resulting from production faults) caused 74% of corrosion damage. Most of the severe chloride-induced corrosion damage in bridges was found in the inner NIB girders, particularly in the support-zones and their vicinity. This can be due to interaction between geometry and exposure. Corrosion of reinforcement in support-zones can impact structural behavior, particularly NIB girder shear performance.

@en

Although the steel–concrete interface (SCI) is widely recognized to influence the durability of reinforced concrete, a systematic overview and detailed documentation of the various aspects of the SCI are lacking. In this paper, we compiled a comprehensive list of possible local characteristics at the SCI and reviewed available information regarding their properties as well as their occurrence in engineering structures and in the laboratory. Given the complexity of the SCI, we suggested a systematic approach to describe it in terms of local characteristics and their physical and chemical properties. It was found that the SCI exhibits significant spatial inhomogeneity along and around as well as perpendicular to the reinforcing steel. The SCI can differ strongly between different engineering structures and also between different members within a structure; particular differences are expected between structures built before and after the 1970/1980s. A single SCI representing all on-site conditions does not exist. Additionally, SCIs in common laboratory-made specimens exhibit significant differences compared to engineering structures. Thus, results from laboratory studies and from practical experience should be applied to engineering structures with caution. Finally, recommendations for further research are made.

@en