Crystalline admixture (CA) is an effective self-healing agent for mortar. However, the effects of crack parameters (i.e. crack width and cracking age) and the service environment on the self-healing behavior of CA-containing mortar are not well understood. Herein, the self-healing behavior of mortar containing a self-developed CA was assessed by testing strength recovery, impermeability recovery, and crack closure in pre-cracked specimens. Three initial crack widths (0.2, 0.3, and 0.4 mm), five cracking ages (3, 7, 14, 28, and 56 days), and four external exposure conditions (humidity chamber, air exposure, water immersion, and wet-dry cycles) are investigated. Furthermore, the influence of different external conditions on the healing products at the region of crack and the pore structure of hardened paste containing CA are studied. The results show that adding 4.54% CA into mortar allows rapid healing of 300 μm-wide cracks. Although wider cracks (400 μm) are more difficult to heal, the sorptivity coefficients of the mortars with 400 μm-wide cracks after healing decrease. When the cracks are produced at an earlier age, the pre-cracked specimens have higher recovery ratios of strength and impermeability after healing, and the specimens pe-cracked at a later age still have acceptable compressive strengths after healing. The analysis shows that the strengths and impermeabilities of pre-cracked mortars containing CA exposed to the four external conditions are all recovered. The best self-healing performance is observed for the specimens exposed to water immersion and wet-dry cycles conditions. Somewhat less good self-healing was observed in the specimens exposed to humid chamber condition, while the worst self-healing performance was in the specimens exposed to air exposure condition. This study provides a theoretical basis for the application of novel CAs in cement-based materials.

@en

This paper presents a novel transparent amplifying intelligent surface (TAIS) architecture for uplink enhancement in indoor-To-outdoor mmWave communications. The TAIS is an amplifier-based transmissive intelligent surface that can refract and amplify the incident signal, instead of only refracting it with adjustable phase shift by most passive reconfigurable intelligent surfaces (RIS). With advanced indium tin oxide film and printing technology, TAIS can be fabricated on the windows without any visual effects. This paper primarily focuses on exploiting the TAIS-based architecture to boost the uplink spectral efficiency (SE) in indoor-To-outdoor mmWave communications. By jointly optimizing the TAIS's phase shift matrix and transmit power of the user equipment, the uplink SE can be maximized by exploiting the nonlinearity in the TAIS's amplification process. The key enabler is that we drive the optimal phase shift matrix that maximizes the SE and deduces its closed-form representation. The SE maximization is then proved to be transferred to the transmit power optimization problem. Another important enabler is that we design a low-complexity algorithm to solve the optimization problem using the difference of convex programming. Moreover, the asymptotic spectral efficiency under nonlinear amplification and power scaling law with infinitely large elements under both the sparse and rich scattering channel models are analyzed. Simulation results show that our proposed TAIS can increase the SE by up to 24.7% as compared to its alternative methods.

@en

This paper presents a novel transparent amplifying intelligent surface (TAIS) architecture for uplink enhancement in indoor-to-outdoor mmWave communications. The TAIS is an amplifier-based transmissive intelligent surface that can refract and amplify the incident signal, instead of only refracting it with adjustable phase shift by most passive reconfigurable intelligent surfaces (RIS). With advanced indium tin oxide film and printing technology, TAIS can be fabricated on the windows without any visual effects. This paper primarily focuses on exploiting the TAIS-based architecture to boost the uplink spectral efficiency (SE) in indoor-to-outdoor mmWave communications. By jointly optimizing the TAIS's phase shift matrix and transmit power of the user equipment, the uplink SE can be maximized by exploiting the nonlinearity in the TAIS's amplification process. The key point is that we drive the optimal phase shift matrix that maximizes the SE and deduces its closed-form representation. The SE maximization is then proved to be transferred to the transmit power optimization problem. Another important aspect is that we design a low-complexity algorithm to solve the problem using the difference of convex programming. Simulations show that our proposed TAIS can increase the SE by up to 32.6% as compared to its alternative methods.@en