The present study proposes a novel model to modify master S-N curves of components according to their load redistribution capability reflected in different boundary conditions (BCs) based on the fracture mechanics analysis. To that end, a comprehensive numerical study was conducted on a Single Edge Notch Bend (SENB) specimen constrained with different kinematic BCs using discrete fatigue crack growth (FCG) simulation. It was observed that BCs indeed can have a significant effect on the crack growth behavior and consequently on the resulting fatigue life under the same nominal loading conditions. The proposed model was applied to the S-N curve of a T-welded joint, and the predicted fatigue life was validated against 3D FCG simulations. Finally, FCG tests were conducted on SENB specimens to experimentally corroborate the effect of BCs on the FCG rate.

@en

Steel Orthotropic Bridge Decks (OBDs) are widely used in long-span and movable bridges. Fatigue resistance analysis plays an important role in the design or assessment of OBDs. One possible fatigue failure is the crack initiating from the weld root of stiffener-to-deck plate connections at crossbeams. A full-scale experimental investigation in this study using a 20 mm thick deck plate with a dimension of 9.4 m × 5.1 m, including three crossbeams, represents the modern designed OBDs. The experiments show an arrest of crack propagation with a final crack depth of approximately 75% of the deck plate thickness. On the contrary, through thickness cracks develop in deck plates of 10 or 12 mm. Hot spot stress based fatigue detail categories (DC) using various failure criteria derived from the tests. Analysis with the effective notch stress shows that the DC has low sensitivity to the amount of weld penetration. The results of analyses with the eXtended Finite Element Method (XFEM), employed to analyse the fatigue crack propagation path and crack arrest, are in line with the experimental study.

@en

Fatigue cracks in the stiffener-to-deck plate connections of orthotropic bridge decks, initiating from the weld toe or root and propagating into the stiffener or weld throat, are experimentally and numerically studied. A statistical analysis of the structural stress is carried out using the experimental data. Automatic welded specimens show a significantly higher fatigue resistance than manual welded ones for both details of the study. Including results in the literature, the characteristic fatigue resistances appear larger than the values in current standards and range between 100 and 160 MPa. A proposal for the fatigue resistance values is given for design purposes. The effective notch stress, averaged strain energy density factor, and fracture mechanics methods are employed to study the sensitivity of the weld toe and root cracks for different (geometrical) variations, such as the lack of weld penetration. Among them, the fracture mechanics method agrees best with the experimental data. With the increase of weld penetration ratios from 75% to 100%, the fracture mechanics predicted fatigue resistances remain approximately equal for the weld toe cracks and increase for the weld root cracks.

@en

Steel Orthotropic Bridge Decks (OBDs) are widely used in the superstructures of movable and long-span bridges. There is a high concentration of stress at many welded connections, which are governing the fatigue performance of OBDs. The fatigue behaviour of the lower end of weld in crossbeam-to-stiffener connection with cut-outs is studied from multiple experimental results obtained from a 48m2 full-scale specimen, as well as finite element simulations. The fatigue resistance of the detail is recommended based on 8 experiments reported in the current study and experiments in the literature using the hot spot stress method. The influence of the load location on the hot spot stress is analysed. The effective notch stress method is used to evaluate the fatigue resistance with different weld profiles.@en

This study derives the fatigue resistance of welded details in orthotropic decks using structural stress (hot-spot stress where possible) based on tests described in literature and tests by the authors. The data are supported with linear elastic fracture mechanics simulations. Details covered are the rib to deck weld, the crossbeam to deck weld and the deck butt weld. High fatigue resistances are found, caused by favourable loading modes (bending and compression) and reduced driving force with the growth of cracks. The technical specification TS 1993-1-901, part of the new generation of Eurocodes, is based on the results of this study.

@en

The orthotropic steel decks (OSDs) are widely used in bridge engineering to support traffic loads. A possible crack, initiating from the weld toe of rib-to-deck welded joint and growing into the deck plate, is studied using linear elastic fracture mechanics. A detailed FE model is created and the results are compared with the fatigue tests published. Good agreement is found between beach marks from experiments and calculated crack fronts in FE. An engineering approach with the crack shape simplified as a semi-ellipse is applied. Geometric correction factors for a hand calculation method is proposed based on the parametric analysis. Using the proposed correction factors, Monte Carlo simulation is carried out with failure criteria defined with respect of the crack depth reaching “50%” of the deck thickness, “75%” of the deck thickness, and the failure criterion “2A FAD” according to BS7910. Predicted results using the failure criterion “75%” show good agreement with experimental data, for 5%, 50%, and 95% survival probabilities. Effects of initial crack shapes and sizes are discussed using the improved hand calculation model. Lower fatigue resistance is found when the initial crack is shallow or large. In addition to the standard weld geometry in which the weld profile is represented by a straight line, concave and convex arc shape weld profiles are studied. Fatigue resistance is improved in the case with assumption of concave arc weld profile. The difference of fatigue resistance between the cases with a straight line and convex arc weld profiles is small.

@en

The orthotropic steel decks are one of the most widely used bridge decks, especially in moveable and long span bridges. Numerous cracks have been detected in existing bridges, mainly in the welded connections. Fatigue performance of the bridge decks governs the design. The crack at the rib-to-deck joint is one of the most representative types. Strict requirements of the configuration of this joint are given in design codes resulting in classification categories based on experimental findings. Fatigue life of the crack initiation and changes of the stress conditions are usually experimentally investigated. However, prediction of the crack propagation and the effect of the cracks on the local stress fields are not possible to be fully understood based on experiments only. In this paper, finite element models are refined around the crack tip using software programs Abaqus and FRANC3D to study the crack propagation of rib-to-deck joint between crossbeams. The results is compared with beach marking tests in literature. Good agreement is found between predicted results and test data for both the crack shapes and loading cycles. The largest SIF range is predicted in the middle of the developed crack. It is then moved to the position 0.19 (relative distance, normalized by the width of the specimen) away from the crack priori to the fracture. During propagation period, structural integrity is affected by the crack and stress redistribution phenomenon is observed.@en

The orthotropic steel decks (OSDs) are one of the most widely used bridge components, especially in moveable and long span bridges. Numerous cracks have been detected in this type of deck in existing bridges, mainly in the welded joints. The fatigue performance of the bridge deck dominates its design. Among them, the crack at the rib-to-deck joint is one of the most representative types. At the crossbeam conjunction, high stress concentration makes the joint more sensitive to fatigue loading. In this paper, finite element models are built using software program Abaqus integrated with FRANC3D. The calculated stress at uncracked stage is validated with measured data obtained from laboratory tests. Afterwards, cracks are inserted at the weld root and the stress intensity factor ranges in mode I (ΔK _I ) are calculated. Parametric analysis with various cracks is carried out. General correction factors are calculated from the finite element calcualtion with the power fit values.

@en