The fabrication process of interdigitated-back-contacted silicon heterojunction (IBC-SHJ) solar cells has been significantly simplified with the development of the so-called tunnel-IBC architecture. This architecture utilizes a highly conductive (p)-type nanocrystalline silicon (nc-Si:H) layer deposited over the full substrate area comprising pre-patterned (n)-type nc-Si:H fingers. In this context, the (p)-type nc-Si:H layer is referred to as blanket layer. As both electrodes are connected to the same blanket layer, the high lateral conductivity of (p)nc-Si:H layer can potentially lead to relatively low shunt resistance in the device, thus limiting the performance of such solar cells. To overcome such limitation, we introduce a thin (<2 nm) full-area molybdenum oxide (MoO_x) layer as an alternative to the (p)nc-Si:H blanket layer. We demonstrate that the use of such a thin MoO_x minimizes the shunting losses thanks to its low lateral conductivity while preserving the simplified fabrication process. In this process, a novel (n)-type nc-Si:H/MoO_x electron collection contact stack is implemented within the proposed solar cell architecture. We assess its transport mechanisms via electrical simulations showing that electron transport, unlike in the case of tunnel-IBC, occurs in the conduction band fully. Moreover, the proposed contact stack is evaluated in terms of contact resistivity and integrated into a proof-of-concept front/back-contacted (FBC) SHJ solar cells. Contact resistivity as low as 100 mΩcm² is achieved, and fabricated FBC-SHJ solar cells obtain a fill factor above 81.5% and open-circuit voltage above 705 mV. Lastly, the IBC-SHJ solar cells featuring the MoO_x blanket layer are fabricated, exhibiting efficiencies up to 21.14% with high shunt resistances above 150 kΩcm². Further optimizations in terms of layer properties and fabrication process are proposed to improve device performance and realize the efficiency potential of our novel IBC-SHJ solar cell architecture.

Transition metal oxide (TMO) thin films exhibit large bandgap and hold great potential for enhancing the performance of silicon heterojunction (SHJ) solar cells by increasing the short-circuit current density significantly. On the other hand, achieving precise control over the electrical properties of TMO layers is crucial for optimizing their function as efficient carrier-selective layer. This study demonstrates a general and feasible approach for manipulating the quality of several TMO films, aimed at enhancing their applicability in silicon heterojunction (SHJ) solar cells. The core of our method involves precise engineering of the interface between the TMO film and the underlying hydrogenated intrinsic amorphous silicon passivation layer by managing the reaction of the TMO on the surface. X-ray photoelectron spectroscopy spectra demonstrate that our methods can modify the oxygen content in TMO films, thereby adjusting their electronic properties. By applying this method, we have successfully fabricated WO_x-based SHJ solar cells with 23.30 % conversion efficiency and V₂O_x-based SHJ solar cells with 22.04 % conversion efficiency, while keeping n-type silicon-based electron-transport layer at the rear side. This research paves the way for extending such interface engineering methods to other TMO materials used as hole-transport layers in SHJ solar cells.

Reducing indium consumption in transparent conductive oxide (TCO) layers is crucial for mass production of silicon heterojunction (SHJ) solar cells. In this contribution, optical simulation-assisted design and optimization of SHJ solar cells featuring MoO_x hole collectors with ultra-thin TCO layers is performed. Firstly, bifacial SHJ solar cells with MoO_x as the hole transport layer (HTL) and three types of n-contact as electron transport layer (ETL) are fabricated with 50 nm thick ITO on both sides. It is found that bilayer (nc-Si:H/a-Si:H) and trilayer (nc-SiO_x:H/nc-Si:H/a-Si:H) as n-contacts performed electronically and optically better than monolayer (a-Si:H) in bifacial SHJ cells, respectively. Then, as suggested by optical simulations, the same stack of tungsten-doped indium oxide (IWO) and optimized MgF₂ layers are applied on both sides of front/back-contacted SHJ solar cells. Devices endowed with 10 nm thick IWO and bilayer n-contact exhibit a certified efficiency of 21.66% and 20.66% when measured from MoO_x and n-contact side, respectively. Specifically, when illuminating from the MoO_x side, the short-circuit current density and the fill factor remain well above 40 mA cm⁻² and 77%, respectively. Compared to standard front/rear TCO thicknesses (75 nm/150 nm) deployed in monofacial SHJ solar cells, this represents over 90% TCO reduction. As for bifacial cells featuring 50 nm thick IWO layers, a champion device with a bilayer n-contact as ETL is obtained, which exhibits certified conversion efficiency of 23.25% and 22.75% when characterized from the MoO_x side and the n-layer side, respectively, with a bifaciality factor of 0.98. In general, by utilizing a n-type bilayer stack, bifaciality factor is above 0.96 and it can be further enhanced up to 0.99 by switching to a n-type trilayer stack. Again, compared to the aforementioned standard front/rear TCO thicknesses, this translates to a TCO reduction of more than 67%.

Silicon heterojunction (SHJ) solar cells have achieved a record efficiency of 26.81% in a front/back-contacted (FBC) configuration. Moreover, thanks to their advantageous high V_OC and good infrared response, SHJ solar cells can be further combined with wide bandgap perovskite cells forming tandem devices to enable efficiencies well above 33%. In this study, we present strategies to realize high-efficiency SHJ solar cells through combined theoretical and experimental studies, starting from the optimization of Si-based thin-film layers to the implementation of electrodes with reduced indium and silver usage. Advanced opto-electrical simulations, which enable comprehensive theoretical understandings of the main physical mechanisms governing carriers’ collection and light management, provide clear pathways for device designs and experimental optimizations. We present the fabricated FBC-SHJ solar cells in both monofacial and bifacial configurations with the best efficiencies of 24.18% and 23.25%, respectively. We point out that to achieve optimum device performance, the compositional materials should be holistically optimized and evaluated as part of the contact stacks with adjacent layers. As an outlook beyond the classical FBC-SHJ solar cell architecture, we propose various novel SHJ-based solar cell architectures. Their potential performance was assessed and compared via rigorous opto-electrical simulations and a maximal efficiency of 27.60% was simulated for FBC-SHJ solar cells featuring localized contacts.