Copoly(2-nonyl-2-oxazoline)-stat-poly(2-dec-9′enyl-2-oxazoline)s can be crosslinked by the thiol-ene reaction with glycol dimercaptoacetate. The copoly(2-oxazoline)-stat-copolyester is tested as dielectric for high-voltage applications, either as unfilled resin or as composite with nanoscaled fillers of silica, alumina, and hexagonal boron nitride. During AC voltage tests, all materials have an average breakdown strength of 45–50 kV mm−1. For DC voltage tests, samples with SiO2 (hBN) have an average breakdown strength of ≈100 (80) kV mm−1, while the unfilled copoly(2-oxazoline) has an average breakdown strength of ≈60 kV mm−1. Permittivity measurements at 20 °C and 50 Hz reveal that all nanocomposites are dielectrics (D = 0.06–0.08), while the unfilled copoly(2-oxazoline)s has a high loss factor of D = 8.43. This phenomenon can be retraced to the phase separation in the crosslinked copolymer, the M-OH functionality of silica and alumina particles, and models of polymer–particle interactions such as the Tanaka model, revealing that the nanofillers reduce the interfacial and dipolar polarizability.@en

Five types of nanofillers, namely, silica, surface-silylated silica, alumina, surface-silylated alumina, and boron nitride, were tested in this study. Nanocomposites composed of an epoxy/amine resin and one of the five types of nanoparticles were tested as dielectrics with a focus on (i) the surface functionalization of the nanoparticles and (ii) the water absorption by the materials. The dispersability of the nanoparticles in the resin correlated with the composition (OH content) of their surfaces. The interfacial polarization of the thoroughly dried samples was found to increase at lowered frequencies and increased temperatures. The β relaxation, unlike the interfacial polarization, was not significantly increased at elevated temperatures (below the glass-transition temperature). Upon the absorption of water under ambient conditions, the interfacial polarization increased significantly, and the insulating properties decreased or even deteriorated. This effect was most pronounced in the nanocomposite containing silica, and occurred as well in the nanocomposites containing silylated silica or non-functionalized alumina. The alternating current (AC) breakdown strength of all specimens was in the range of 30 to 35 kV·mm−1. In direct current (DC) breakdown tests, the epoxy resin exhibited the lowest strength of 110 kV·mm−1; the nanocomposite containing surface-silylated alumina had a strength of 170 kV·mm−1. In summary, water absorption had the most relevant impact on the dielectric properties of nanocomposites containing nanoparticles, the surfaces of which interacted with the water molecules. Nanocomposites containing silylated alumina particles or boron nitride showed the best dielectric properties in this study.@en

Radical induced cationic frontal polymerization (RICFP) is an extremely powerful and elegant alternative curing technique that allows cationic bulk curing of epoxy resins with very little energy consumption, as well as curing in compart-
ments that are not readily accessible. We recently introduced a bisphenol-A diglycidylether (BADGE) based system that allows the bubble-free photocuring of this widely used epoxy resin. In this article, we describe the high storage stability and possibili-ties to influence the curing speed via the initiator concentra-
tions of different formulations. These properties allow the adjustment of the frontal polymerization to ones need. We also show that the (thermo)mechanical and electrical properties of frontal cured epoxy polymers compares favorably with those of state of the art material. Finally, different strategies to over-
come the challenges on producing epoxy resin based mica
composites via RICFP are presented.
@en