Sr is known to transform the morphology of the eutectic silicon phase as well as the Fe-rich β phase in Al-Si alloys, improving their mechanical properties. However, little is known about the effect Sr has on the (local) corrosion properties of aluminium alloys. This study investigates the effect of Sr addition to a modified AA3003 heat exchanger material on the morphology of the different phases present, especially the Fe-rich phases, as well as on the (local) corrosion properties of this material. This work reports the formation of a Sr-rich phase, which slightly increases the macrohardness of the material. The Fe-rich phases are not shown to be refined/influenced by the addition of Sr Potentiodynamic polarization experiments showed an increase in pitting potential by increasing the amount of Sr in the material up to 0.4 wt.%. Nevertheless, the analysis of the corrosion morphology revealed that the Sr-containing particles did not contribute to the corrosion process despite their cathodic behaviour compared to the Al matrix as measured by Scanning Kelvin Probe Force Microscopy. This behaviour was attributed to the thicker oxide layer found on the Sr-rich particles.

@en

Aluminum alloy (AA) 3003 is widely used as fin and tube material in heat exchangers. In these heat exchangers, the tube and fin material are brazed together by means of an AA4xxx alloy. In this study, the effect of a simulated brazing step on the microstructure and corrosion behavior of a twin roll casted (TRC) AA3003 was studied. In particular, the effect of simulated brazing on the corrosion properties of the centre line segregation (CLS) of alloying elements and the interaction of the intermetallic particles with the surrounding matrix is explored. It is shown that the cross sections are significantly more active than the surface of the TRC AA3003, revealing the importance of the CLS on the corrosion behavior. Furthermore, it is shown that the number of pits and their depths decreased considerably on the exposed cross sections after simulated brazing, especially near the CLS. Scanning Kelvin probe force microscopy measurements show that after the simulated brazing step the Volta potential difference between the intermetallic particles and the matrix reduced significantly. This change in the Volta potential could be caused by the slight increase of Si content in the matrix.@en