An ethanol gas sensor based on carbon nanofibers (CNFs) with various densities and nanoparticle functionalization was investigated. The CNFs were grown by means of a Plasma-Enhanced Chemical Vapor Deposition (PECVD), and the synthesis conditions were varied to obtain different number of fibers per unit area. The devices with a larger density of CNFs lead to higher responses, with a maximal responsivity of 10%. Furthermore, to simultaneously improve the sensitivity and selectivity, CNFs were decorated with gold nanoparticles by an impaction printing method. After metal decoration, the devices showed a response 300% higher than pristine devices toward 5 ppm of ethanol gas. The morphology and structure of the different samples deposited on a silicon substrate were characterized by TEM, EDX, SEM, and Raman spectroscopy, and the results confirmed the presence of CNF decorated with gold. The influence of operating temperature (OT) and humidity were studied on the sensing devices. In the case of decorated samples with a high density of nanofibers, a less-strong cross-sensitivity was observed toward a variation in humidity and temperature.@en

In this paper, we study the influence of two key factors, temperature, and humidity, on gas sensors based on titanium dioxide nanowires synthesized at 4 different temperatures and with different morphology. The samples' structure are investigated using SEM, XRD and FTIR analysis. The effects of humidity and temperature are studied by measuring the resistance and gas response when exposed to ethanol. At room temperature, we observed a 15% sensitivity response to 100 ppm of ethanol vapor and by increasing the operating temperature up to 180 C, the response is enhanced by two orders of magnitude. The best operating temperature for the highest gas response is found to be around 180 C. Also, it was observed that every nanowire morphology has its own optimum operating temperature. The resistance of sensors is increased at higher Relative Humidity (RH). Besides, the response to ethanol vapor experiences a gradual increase when the RH rises from 10% to 60%. On the other hand, from 60% to 90% RH the gas response decreases gradually due to different mechanisms of interaction of the TiO2 with H2O and ethanol molecules.

@en

Carbon nanotubes (CNTs) have shown promising results for gas sensing due to their high surface area. Since humidity has a great impact on the electrical conductivity of resistive CNT gas sensors, we have investigated the change of humidity on their sensing properties. In this study, we fabricated vertically aligned CNT-based gas sensors for the detection of volatile organic compounds. The morphologies and phase structures of the fabricated samples were characterized using scanning electron microscopy (SEM), X-ray diffraction (XRD) and Fourier-transform infrared spectroscopy (FT-IR), confirming the presence of CNT with some surface impurities. It was found that a relative humidity increase from 10% to 80% can reduce the electrical conductivity of the sensor by around 4%. On the other hand, for a humidity above 80% the conductivity increased slightly. The fabricated device has been used as a gas sensor for volatile organic compounds, and the cross-sensitivity to humidity was investigated. It was found that in the fabricated sensors, a change in humidity up to 80% results in a 40% decrease in the response for the studied organic compounds.@en