Detection of hazardous toxic gases for air pollution monitoring and medical diagnosis has attracted the attention of researchers in order to realize sufficiently sensitive gas sensors. In this paper, we fabricated and characterized a Titanium dioxide (TiO2)-based gas sensor enhanced using the gold nanoparticles. Thermal oxidation and sputter deposition methods were used to synthesize fabricated gas sensor. X-ray diffraction analysis was used to determine the anatase structure of TiO2samples. It was found that the presence of gold nanoparticles on the surface of TiO2enhances the sensitivity response of gas sensors by up to about 40%. The fabricated gas sensor showed a sensitivity of 1.1, 1.07 and 1.03 to 50 ppm of acetone, methanol and ethanol vapors at room temperature, respectively. Additionally, the gold nanoparticles reduce 50 s of response time (about 50% reduction) in the presence of 50 ppm ethanol vapor; and we demonstrated that the recovery time of the gold decorated TiO2sensor is less than 40 s. Moreover, we explain that the improved performance depends on the adsorption-desorption mechanism, and the chemical sensitization and electronic sensitization of gold nanoparticles.

@en

We propose an induction link based on overlapping arrays to eliminate blank spots on the electromagnetic field for moving object applications. We use two arrays of four aligned coils that have a 50% overlap between the two plates. This mechanism compensates for the internal coil power drop at positions in the boundaries between two adjacent external coils. We showed that if these plates are excited, a uniform electromagnetic field is created in the movement direction of the moving object. This uniform electromagnetic field distribution will result in a constant receiving power at all points in the path of the moving internal coil with the same power consumption of one coil excitation. Power delivery to the moving object tolerance reaches 10% at most, while, in non-overlapped scenarios, it is approximately 50%. In addition, according to the theoretical calculations, printed circuit coils (PCB) for the array are designed for maximum efficiency. We found that the change in distance and dimensions of the receiver coil has a linear effect on power and efficiency. Moreover, a Specific Absorption Rate (SAR) simulation was performed for biocompatibility. In this paper, we investigate and record a 68% electrical power efficiency for the fabricated system. The array consists of eight transmitters coils of the same size and shape and a receiver coil at a distance of 4 cm. Furthermore, the fabricated coil has shown improved efficiency compared to similar studies in the literature and introduces a promising structure for bio-test applications.@en

Wireless power is one of the new promising technologies for IoT applications. The use of arrays for power transfer to free-moving objects has revolutionized wireless power transmission (WPT) applications. Herein, we present an extendable platform for transmitting power to a moving object receiving power from an array. The transmitter (TX) consists of two overlapping layers of square planar coils rotated 45 degrees to each other to provide the best electromagnetic flux coverage. Each layer consists of four coils to further control the power supply to the small receiver (RX) coil. This overlapping star-shaped array is stimulated automatically by a power amplifier. This smart stimulation can deliver uniform power to the receiver regardless of rotation and misalignment inconsistencies by using the geometry of the transmitter array. Moreover, by changing the direction of the current of each small square component in each array using the flower-shaped current, a receiver coil perpendicular to the transmitter’s plate can obtain power comparable with conventional structures. We use ADS-HFSS simulation to verify the fabrication and measurement results. The proposed transmitter achieves an average of 18.2% power transfer efficiency (PTE) to RX and at 90° angular misalignment, 11.5% PTE, while the conventional structure transfers no power to the perpendicular RX coil. A future application of the transmitter can be the investigation of the neurobehavioral of free-moving animals and brain–machine interface studies in medicine. @en

A microfluidic-based gas sensor was chosen as an alternative method to gas chromatography and mass spectroscopy systems because of its small size, high accuracy, low cost, etc. Generally, there are some parameters, such as microchannel geometry, that affect the gas response and selectivity of the microfluidic-based gas sensors. In this study, we simulated and compared 3D numerical models in both simple and serpentine forms using COMSOL Multiphysics 5.6 to investigate the effects of microchannel geometry on the performance of microfluidic-based gas sensors using multiphysics modeling of diffusion, surface adsorption/desorption and surface reactions. These investigations showed the simple channel has about 50% more response but less selectivity than the serpentine channel. In addition, we showed that increasing the length of the channel and decreasing its height improves the selectivity of the microfluidic-based gas sensor. According to the simulated models, a serpentine microchannel with the dimensions W = 3 mm, H = 80 µm and L = 22.5 mm is the optimal geometry with high selectivity and gas response. Further, for fabrication feasibility, a polydimethylsiloxane serpentine microfluidic channel was fabricated by a 3D printing mold and tested according to the simulation results@en

An ethanol gas sensor based on carbon nanofibers (CNFs) with various densities and nanoparticle functionalization was investigated. The CNFs were grown by means of a Plasma-Enhanced Chemical Vapor Deposition (PECVD), and the synthesis conditions were varied to obtain different number of fibers per unit area. The devices with a larger density of CNFs lead to higher responses, with a maximal responsivity of 10%. Furthermore, to simultaneously improve the sensitivity and selectivity, CNFs were decorated with gold nanoparticles by an impaction printing method. After metal decoration, the devices showed a response 300% higher than pristine devices toward 5 ppm of ethanol gas. The morphology and structure of the different samples deposited on a silicon substrate were characterized by TEM, EDX, SEM, and Raman spectroscopy, and the results confirmed the presence of CNF decorated with gold. The influence of operating temperature (OT) and humidity were studied on the sensing devices. In the case of decorated samples with a high density of nanofibers, a less-strong cross-sensitivity was observed toward a variation in humidity and temperature.@en

Here we investigated a novel layer-based optimization technique to improve the performance of a CZTSe solar cell. By using this technique, the optical behavior and electrical properties of the proposed solar cell improved significantly as a result of the changes in the layer specifications and the layer materials. The structure of the cell consisted of an absorber laid on a conducting layer and covered by Indium Tin Oxide (ITO), with ZnO on its top surface. Due to the employment of the CSLO technique, a p+pn junction was formed between the absorber and window layers, which provided a lower recombination rate by transmitting more electrons and holes to the contacts. In addition, the main important parameters affecting the solar cell’s performance such as layer thickness, carrier lifetime, and total effect density were investigated. According to the results, the proposed CZTSe solar cell achieved a 32.6% and 79.5% efficiency and fill factor, respectively—which in comparison to a conventional solar cell is remarkable. Moreover, hybrid structures made by utilizing CZTS-based, Ge-based Cu2ZnGeSe4, and Si-based Cu2ZnSiSe4 with the proposed CZTSe-based solar cell were implemented and better results were achieved, yielding an efficiency of about 42, 50, and 34% and a fill factor of 66, 55, and 42%, respectively, due to the materials’ properties.@en

In this paper, we study the influence of two key factors, temperature, and humidity, on gas sensors based on titanium dioxide nanowires synthesized at 4 different temperatures and with different morphology. The samples' structure are investigated using SEM, XRD and FTIR analysis. The effects of humidity and temperature are studied by measuring the resistance and gas response when exposed to ethanol. At room temperature, we observed a 15% sensitivity response to 100 ppm of ethanol vapor and by increasing the operating temperature up to 180 C, the response is enhanced by two orders of magnitude. The best operating temperature for the highest gas response is found to be around 180 C. Also, it was observed that every nanowire morphology has its own optimum operating temperature. The resistance of sensors is increased at higher Relative Humidity (RH). Besides, the response to ethanol vapor experiences a gradual increase when the RH rises from 10% to 60%. On the other hand, from 60% to 90% RH the gas response decreases gradually due to different mechanisms of interaction of the TiO2 with H2O and ethanol molecules.

@en

Carbon nanotubes (CNTs) have shown promising results for gas sensing due to their high surface area. Since humidity has a great impact on the electrical conductivity of resistive CNT gas sensors, we have investigated the change of humidity on their sensing properties. In this study, we fabricated vertically aligned CNT-based gas sensors for the detection of volatile organic compounds. The morphologies and phase structures of the fabricated samples were characterized using scanning electron microscopy (SEM), X-ray diffraction (XRD) and Fourier-transform infrared spectroscopy (FT-IR), confirming the presence of CNT with some surface impurities. It was found that a relative humidity increase from 10% to 80% can reduce the electrical conductivity of the sensor by around 4%. On the other hand, for a humidity above 80% the conductivity increased slightly. The fabricated device has been used as a gas sensor for volatile organic compounds, and the cross-sensitivity to humidity was investigated. It was found that in the fabricated sensors, a change in humidity up to 80% results in a 40% decrease in the response for the studied organic compounds.@en