Fibre bridging can significantly enhance delamination resistance making the use of a single Paris resistance curve to determine fatigue crack growth insufficient. An empirical Paris-type relation has been developed in a previous study to take fibre bridging into account in fatigue delamination growth. This relation was developed by correlating the Paris constants C and n to the amount of fibre bridging. This paper provides a further investigation on the interface configuration effect on fatigue delamination growth, illustrating the significance of fibre bridging. The results demonstrated that more bridging fibres can be generated in a multidirectional interface, making both log(C) and n significantly depend on fibre bridging. Thus, the method proposed in the previous study is further extended to take into account of the interface configuration effect.@en

This paper aims to investigate stress ratio effect on fibre bridging significance in mode I fatigue delamination growth of composite materials. Fatigue resistance curves (R-curves) of different stress ratios are determined and compared with the quasi-static R-curve. The fatigue R-curve of a high stress ratio is similar to the quasi-static results. However, fatigue resistance of a low stress ratio is smaller than quasi-static resistance. These indicate that fibre bridging significance is stress ratio dependent. More bridging fibres can be generated in delamination of a high stress ratio, as compared to that of a low stress ratio. This can lead to fatigue bridging laws are stress ratio dependent and fatigue delamination is block load sequence dependent.@en