Here we investigate the adhesive properties of Selective Laser Melted (SLM) titanium surfaces in metal-composite cobonded joints without any prior surface treatment, to explore the inherent surface roughness of SLM parts to potentially create strong adhesive bonds. Double Cantilever Beam (DCB) tests were carried out to assess the joints mode I fracture toughness involving untreated SLM titanium and woven Carbon Fibre Reinforced Polymer (CFRP) adherends, co-bonded with an epoxy film adhesive. The same type of DCB joints, but now with sandblasted SLM titanium adherends, were tested to compare the adhesion strength of the untreated SLM surface versus the sandblasted surface. The findings reveal that joints with untreated SLM titanium adherends exhibit similar toughness to those with sandblasted SLM titanium adherends, indicating that the surface morphology of as-printed SLM titanium is suitable for manufacturing robust adhesive joints. The elimination of the surface treatment in the manufacturing of adhesive joints with SLM adherends could increase the interest of many industrial fields towards the use of adhesive bonding over other joining techniques.@en

Parts manufactured with Laser Powder Bed Fusion (LPBF) are drawing interest in the adhesive joints research because of their high surface roughness, which is usually associated with good adhesion. This work aims to assess the adhesion strength of the inherent surface morphology of LPBF manufactured titanium.
Double Cantilever Beam (DCB) tests were carried out to determine the mode I fracture toughness of joints comprising as-printed titanium (Ti6Al4V) adherends, namely titanium-titanium secondary bonded and titanium-Carbon Fibre Reinforced Polymer (CFRP) co-bonded joints. The effect of high-temperature oxidation on the fracture toughness was also evaluated by testing a batch of joints in which the titanium underwent a post-printing thermal treatment. The as-printed specimens were compared to the same type of joints but with sandblasted titanium adherends to evaluate the effect of this surface pre-treatment on the value of fracture toughness.
The results indicate that non-oxidised titanium joints with untreated adherends had an average of 11% higher fracture toughness than their sandblasted counterparts. On the other hand, sandblasting proved beneficial for oxidised joints, increasing the fracture toughness by 64% on average over the untreated samples.@en