Layered double hydroxides (LDHs) can shield polymeric materials from UV light, which allows reducing material aging and erosion damage of bituminous pavement under physical and chemical action. In this study, the physicochemical properties, aging resistance, and erosion resistance to the aqueous solution of LDHs modified bitumen mastic (BM) were characterized by Fourier-transform infrared spectroscopy, basic physical tests, viscosity tests, a dynamic shear rheometer, and a bending beam rheometer. The results show that few chemical reactions occurred between LDHs and BM, indicating that a physical mechanism underlay the modification of BM by LDHs. Moreover, LDHs could increase the flow activation energy of BM by 0.12%, increase the high failure temperature from 69.07 °C to 71.07 °C, and decrease the low failure temperature from −10.50 °C to −12.39 °C. Therefore, LDHs could slightly reduce the temperature sensitivity of BM, while slightly enhancing the high and low-temperature rheological properties of BM. Compared with short-term aging and long-term aging, LDHs could significantly improve the UV aging resistance of BM. The above results are consistent with previous studies of LDHs-modified bitumen. Furthermore, water and pH 3 acidic solutions had the greatest degree of erosion to BM, and LDHs could improve the resistance to aqueous solutions. Overall, this study can help to investigate the effects of various environmental factors on the performance of LDHs modified bitumen pavements during long-term use.@en

During the service period, asphalt materials are affected by various natural factors, including heat, ultraviolet light, oxygen and moisture, etc., resulting in the reduction of pavement performance, the increase of pavement distress and shortening of service life. This study aims to investigate the aging performance of asphalt under multiple aging conditions of heat, UV and aqueous solution. Thermal-oxygen aging, UV aging and hydrostatic erosion tests were carried out sequentially on asphalt. The rheological properties, chemical structure and element composition of asphalt were characterized before and after aging, and the effect mechanism of multiple conditions was discussed. The results show that the multiple conditions of heat and UV can increase the rutting resistance and weaken the cracking resistance of asphalt. However, the effect degree of UV decreases gradually with the deepening of aging degree. Additionally, the effect of water on the physicochemical properties is less than that of UV; however, water can increase the sensitivity of physicochemical properties to UV. In summary, this study explored the short-term cycling effect of heat, light and water on asphalt and provided an idea for simulation test of asphalt under multiple aging condition.

@en