Carbon-supported nickel and nitrogen co-doped (Ni-N-C) catalysts have been extensively studied as selective and active catalysts for CO2 electroreduction to CO. Most studies have focused on adjusting the coordination structure of Ni-Nx active sites, while the impact of the carbon supports has often been overlooked. In this study, a series of Ni-N-C catalysts on different carbon supports, including carbon black (CB), multi-walled carbon nanotubes (CNT), and activated nitrogen-doped biochar (ANBC), were synthesized using a ligand-mediated method. The effect of the carbon support on the electrocatalytic performance for CO2 reduction was investigated at both low current densities, in a H-cell, and high current densities, in a MEA electrolyzer. All of the prepared Ni-N-C catalysts show good faradaic efficiencies (FE) toward CO production (up to ∼90 %), however, the onset potentials and partial current densities for CO production vary greatly. The textural properties of the carbon support and the distribution of Ni-Nx active sites on the carbon support are demonstrated as the main factors behind the performance differences. In particular, hierarchical porous structures with a large specific surface area are helpful to facilitate mass transport and improve the dispersion of active sites, which allows for a better CO2 reduction performance of Ni-N-ANBC compared to Ni-N-CB and Ni-N-CNT. This study demonstrates the importance of the carbon support for Ni-N-C catalysts and provides new insights into the design of efficient Ni-N-C catalysts for the CO2RR.@en

Extending the lifetime of electrocatalytic materials is a major challenge in electrocatalysis. Here, we employ atomic layer deposition (ALD) to coat the surface of carbon black supported platinum nanoparticles (Pt/CB) with an ultra-thin layer of silicon dioxide (SiO2) to prevent deactivation of the catalyst during H2 evolution. Our results show that after an accelerated durability test (ADT) the current density at −0.2 V vs. reversible hydrogen electrode (RHE) of the unprotected Pt/CB catalyst was reduced by 34%. By contrast, after coating the Pt/CB catalyst with 2 SiO2 ALD cycles, the current density at the same potential was reduced by 7% after the ADT procedure, whereas when the Pt/CB sample was coated with 5 SiO2 ALD cycles, the current density was reduced by only 2% after the ADT. Characterization of the Pt particles after electrochemical testing shows that the average particle size of the uncoated Pt/CB catalyst increases by roughly 16% after the ADT, whereas it only increases by 3% for the Pt/CB catalyst coated with 5 cycles of SiO2 ALD. In addition, the coating also strongly reduces the detachment of Pt nanoparticles, as shown by a strong decrease in the Pt concentration in the electrolyte after the ADT. However, 20 cycles of SiO2 ALD coating results in an over-thick coating that has an inhibitory effect on the catalytic activity. In summary, we demonstrate that only a few cycles of SiO2 ALD can strongly improve the stability of Pt catalyst for the hydrogen evolution reaction.@en

This dissertation explores the integration of clean energy and electrochemical CO2 reduction to address environmental issues. Metal-free nitrogen-doped carbon materials, derived from renewable biomass, emerge as efficient catalysts for CO2 reduction, offering sustainability and cost-effectiveness. Chapters delve into methods of N-doped biochar production, activation strategies, structure-performance relationships, catalyst performance in the presence of impurities, and the use of N-doped biochar as a carbon support for Ni-N-C catalyst synthesis. Results highlight the importance of physicochemical properties in enhancing CO2 reduction performance. The catalysts demonstrate resilience to SO2 impurities, outperforming benchmark electrodes, and showcase promise for sustainable CO2 reduction.@en

N-doped carbon materials can be efficient and cost-effective catalysts for the electrochemical CO₂ reduction reaction (CO₂RR). Activators are often used in the synthesis process to increase the specific surface area and porosity of these carbon materials. However, owing to the diversity of activators and the differences in physicochemical properties that these activators induce, the influence of activators used for the synthesis of N-doped carbon catalysts on their electrochemical performance is unclear. In this study, a series of bagasse-derived N-doped carbon catalysts is prepared with the assistance of different activators to understand the correlation between activators, physicochemical properties, and electrocatalytic performance for the CO₂RR. The properties of N-doped carbon catalysts, such as N-doping content, microstructure, and degree of graphitization, are found to be highly dependent on the type of activator applied in the synthesis procedure. Moreover, the overall CO₂RR performance of the synthesized electrocatalysts is not determined only by the N-doping level and the configuration of the N-dopant, but rather by the overall surface chemistry, where the porosity and the degree of graphitization are jointly responsible for significant differences in CO₂RR performance.

@en

Nitrogen-doped (N-doped) carbon catalysts have been widely studied for electrochemical CO₂ reduction to CO. However, the correlation between the physicochemical properties of N-doped carbon catalysts and their electrocatalytic performance for the CO₂RR is still unclear. Herein, a series of N-doped biochar catalysts with different physicochemical properties were synthesized by tuning the carbonization temperature and N-doping level and used for the CO₂RR to analyze the structure-performance relationship. The prepared catalysts exhibited massive differences in maximum faradaic efficiency to CO from 26.8 to 94.9% at around −0.8 to −0.9 V vs RHE. In addition, we find that simply increasing the specific surface area and N-doping level of the catalysts does not effectively improve the catalytic performance for the CO₂RR. A multivariate correlation analysis reveals a negative correlation between the N-doping content and the electrochemical performance. The porous structural properties exhibit a positive correlation to the FE_CO but almost no correlation to j_CO. Interestingly, improving the degree of graphitization, surface hydrophobicity, the abundance of defects, and optimizing the porosity of the N-doped biochar catalyst can efficiently enhance the catalytic performance for the CO₂RR. We conclude that comprehensively analyzing the synergistic effect of various properties of N-doped biochar is critical to reveal structure-activity relationships.

@en

Most research into electrochemical CO2 conversion focusses on improving electrode materials, but neglects the role of the electrolyte. We show the buffer influence on the selectivity of a bimetallic gold–palladium electrode in an effort to elucidate observed inconsistencies between different studies. While hydrocarbons are produced in the phosphate buffer, they remain absent in the bicarbonate buffer, showing that the electrolyte choice plays a crucial role in the selectivity of the electrode.@en

Preparing supported nanoparticles with a well-defined structure, uniform particle size, and composition using conventional catalyst synthesis methods, such as impregnation, precipitation, and deposition-precipitation is challenging. Furthermore, these liquid phase methods require significant solvent consumption, which has sustainable issues and requires complex purification processes, usually leaving impurities on the catalyst, affecting its selectivity and activity. In this work, we employed atomic layer deposition (ALD, a vapor phase synthesis method) to synthesize electrocatalysts with well-controlled core-shell and alloy structures for CO₂ reduction to formic acid. With this approach, the structural control of the catalysts is down to the atomic scale, and the effect of core-shell and alloy structure on Pt−Pd bimetallic catalysts has been investigated. It is shown that the Pt−Pd alloy catalyst displays a 46 % faradaic efficiency toward formic acid, outperforming Pt@Pd and Pd@Pt core-shell structures that show faradaic efficiencies of 22 % and 11 %, respectively. Moreover, both core-shell bimetallic catalysts (Pd@Pt and Pt@Pd) are not stable under electroreduction conditions. These catalysts restructure to more thermodynamically stable structures, such as segregated clusters or alloy particles, during the electrochemical reduction reaction, altering the catalytic selectivity.

@en