This article describes the fabrication of MgF₂ and MgO thin-film-based optical filters and compares the optical transmission of the filters over UV. The MgF₂ thin-films were deposited by use of an e-beam technique and their optical properties were characterised by ellipsometry. The effect of substrate temperature on the optical properties was studied. The MgF₂ optimum refractive indices were obtained with a substrate temperature between 200 °C and 300 °C. Optical simulations were performed to compare the performance of MgF₂ and MgO in the fabrication of near-UV narrow bandpass optical filters. While MgO-based optical filters result in a higher transmittance peak intensity, especially at 350 nm, the MgF₂ optical filters are narrower, present lower values of FWHM, a mean value of 20 nm. This feature could be especially relevant for specific applications on fluorescent optical sensors. Finally, a Fabry-Perot based on a MgF₂/TiO₂ optical filter was deposited, using an e-beam technique for the MgF₂ thin-films and RF-sputtering technique for the TiO₂ thin-films. The MgF₂/TiO₂ optical filter peak transmittance is approximately 70% close to 400 nm, as expected. The results are discussed with focus on applications in fluorescent optical sensors for peaks at 350, 370, 380 and 400 nm, respectively.

@en

The integration of the narrow band imaging (NBI) technique in highly miniaturized minimally invasive medical devices is presented. NBI provides a more reliable sensing performance for in vivo studies on tissues as compared to approaches based on white light illumination. NBI uses a selective filtered light with peak transmission at 415 (blue) and 540 nm (green). The blue light improves the visualization of the superficial mucosal layer, while the deeper penetration of the green light highlights the vascular patterns of the subepithelial vessels. The optical filters are based on a multilayer thin-film stack, using the Fabry-Perot configuration with titanium dioxide (TiO2) and silicon dioxide (SiO2). The blue light-emitting diode (LED) combined with the blue filter results in a maximum central wavelength at 414 nm, full-width half-maximum (FWHM) of 19 nm and maximum relative transmittance of 21%. The green LED combined with the green filter yields maximum peak intensity at 536 nm, FWHM of 30 nm, and maximum relative transmittance of 35%. RF-sputtering was used for the deposition of NBI optical filters. The refractive index and extinction coefficient of the TiO2 and SiO2 thin films were characterized and the green and blue filter designs were experimentally validated.@en