There is a global need for optimizing the use of water that has resulted from increased demand due to industrial development, population growth, climate change and the pollution of natural water resources. One of the solutions is to use reclaimed water in industrial applications that do not require water of potable quality, such as cooling water. However, for cooling water, (treated) wastewater’s hardness is too high, apart from having a high load of suspended solids and organic matter. Therefore, a combination of softening with ceramic micro-filtration was proposed for treating wastewater treatment effluent containing fouling agents for potential use in industrial cooling systems. The effectiveness of the softening process on model-treated wastewater with calcium hydroxide in the presence of phosphate and sodium alginate was first evaluated using jar tests. Furthermore, membrane fouling was studied when filtering the softened water. The results showed that the inhibition of calcium carbonate precipitation occurred when inorganic substances, such as phosphate and organic compounds, were present in the water. The fouling of the membranes due to sodium alginate in water was only slightly negatively affected when combined with softening and phosphate. Therefore, this combination of treatments could be potentially helpful for the post-treatment of secondary effluent for cooling systems.@en

Experiments were conducted to evaluate the possibilities of using treated wastewater for the production of unreinforced concrete blocks. Compressive strength, water absorption and morphology tests of concrete blocks, produced from different makeups of mixing water, drinking water, drinking water spiked with ammonium and phosphate, and the effluent of the city’s wastewater treatment plant, were evaluated. Results showed that the compressive strength of blocks manufactured using treated wastewater was as high as of the blocks produced using drinking water. Ammonium, phosphate and chlorine were found not to have a negative effect on the strength of the blocks. Water absorption tests confirmed the results of the compressive strength, as lower humidity was found in cases of higher strength. In the process of cement hydration, crystals of calcium silicate and calcium hydroxide were observed by morphology tests. From the variability in the results, it could be concluded that the quality of the mixing water was not the only factor that influenced the strength of the unreinforced concrete blocks. The observed differences in strength could, for example, also be attributed to the manufacturing process.

@en

The increasing world population and growth of industrial development lead to growing water scarcity that, combined with deficient sanitation services, represents serious challenges, particularly in regions like sub-Saharan Africa. Water reclamation is a promising approach to reduce water scarcity, serving as a driving force for better sanitation services and protecting the environment by treating sewage and redistributing for the benefit of other water-dependent applications (e.g., industries). This paper aims to give an overview of the global trends on water reclamation, with a focus on industrial use, and to derive lessons for implementation of water reclamation projects in sub-Saharan Africa. Findings show that extensive experience exists in technology and management practices that can allow successful implementation of water reclamation projects in the region. Under the conditions of deficient sanitation services and low levels of technical expertise, the main challenge is to develop a framework that can facilitate the integration of social and technological methodologies and help in introducing water reclamation in water allocation planning, including the development of specific legislation for industrial water use and disposal.

@en