This work investigates hygrothermal aging degradation of unidirectional glass/epoxy composite specimens through a combination of experiments and numerical modeling. Aging is performed through immersion in demineralized water. Interlaminar shear testes are performed after multiple conditioning times and after single immersion/redrying cycles. Degradation of the fiber-matrix interface is estimated using single-fiber fragmentation tests and reverse modeling combining analytical and numerical models. A fractographic analysis of specimens aged at 50°C and 65°C is performed through X-ray computed tomography. The aging process is modeled using a numerical framework combining a diffusion analysis with a concurrent multiscale model with embedded hyper-reduced micromodels. At the microscale, a pressure-dependent viscoelastic/viscoplastic model with damage is used for the resin and fiber-matrix debonding is modeled with a cohesive-zone model including friction. A comparison between numerical and experimental results is performed.

@en

This paper investigates the viscoelastic/viscoplastic/fracture behavior of an epoxy resin. A state-of-the-art pressure-dependent elastoplastic constitutive model (Melro et al. 2013) is expanded to include viscoelasticity, viscoplasticity and a modified damage formulation with linear softening and shrinking pressure-dependent fracture surface. A water plasticization model with a single degradation factor is proposed. A set of new quasi-static and fatigue experiments is used to calibrate the model and assess its predictive capabilities. The model correctly represents the rate dependent plasticity and fracture initiation behavior of the studied epoxy. The stiffness and strength degradations after plasticization are also accurately captured. The model is found to be less suitable in reproducing the measured loading-unloading behavior, which displayed strong nonlinearity in combination with limited permanent deformation. Nevertheless, reasonably accurate fatigue life predictions in the low-cycle regime are obtained.@en

A combined experimental and numerical investigation is conducted on the anisotropic water diffusion behaviour of unidirectional glass/epoxy composites. Experimental diffusivity values are obtained by immersing thin material slices for each of its planes of orthotropy extracted from a thick composite panel and interphase measurements are performed using thermal analysis. In order to elucidate the observed anisotropy, the diffusion process is modelled at the microscale using a representative volume element (RVE) of the material with random fibre distribution. Water concentration gradients are applied to the micromodel and a homogenisation procedure is used to retrieve the macroscopic diffusivity coefficients. The influence of the interphase around the fibres on the diffusion process is modelled by making the matrix diffusivity a function of the distance to the nearest fibre using a level set field. The models are used to fit the experimental data and test a number of hypotheses that may explain the observed anisotropy. The effect of fibres acting as barriers for water movement is found to partially explain the observed transverse diffusivity. However, a fit is only obtained by allowing faster diffusivity at the interphase. In the longitudinal direction, a fit can only be found by allowing for orthotropic interphase diffusivity.

@en