Thermodynamic modeling and experimental study of alkali-activated slag paste

Conference paper (2016)

Authors

Y. Zuo Materials and Environment - CEG
Marija Nedeljković Materials and Environment - CEG
K. Arbi Ghanmi Materials and Environment - CEG
G. Ye Materials and Environment - CEG
Research Group
Materials and Environment (CEG) (TU Delft)
Copyright: © 2016 Y. Zuo, Marija Nedeljković, K. Arbi Ghanmi, G. Ye
More Info
expand_more

Published Date

2016

Language

English

Reuse Rights

Other than for strictly personal use, it is not permitted to download, forward or distribute the text or part of it, without the consent of the author(s) and/or copyright holder(s), unless the work is under an open content license such as Creative Commons.

Faculty

Civil Engineering & Geosciences

Department

Materials- Mechanics- Management & Design

Research Group

Materials and Environment

Abstract

A newly developed thermodynamic approach was introduced from the literature to investigate the influence of NaOH content on the hydrate assemblage and chemistry of aqueous solution of activated slag paste (Na2O/slag=4%, 6% and 8%). The ICP-OES test was performed to obtain the aqueous species profiles such as Si, Ca, Al and Na etc. The elemental concentrations in aqueous solution show a similar trend between thermodynamic calculations and experimental results. The modeling results showed that the influence of NaOH content on the uptake of Na into the primary reaction products and chemical shrinkage depends on slag reaction extent and NaOH content. The NaOH content does not show an obvious influence on the porosity development. The volume fraction of primary products in total products is between 40% and 60%, and particularly increases slightly after a certain degree of reaction for activated slag with Na2O/slag=4% and 6%. The volume ratio between total products and reacted slag is around 1.5~1.7, smaller than the value from 2.06 to 2.2 reported for Portland cement.