Direct ink writing technique is used to 3D print Ti-metal–organic framework (MOF) NH₂-MIL-125 mixed with boehmite dispersal. Pt is also deposited onto 3D-printed monolith using atomic layer deposition (ALD) to offer additional catalytic sites. The Ti-MOF-derived powder sample and the pyrolyzed 3D-printed monolith samples are evaluated for photocatalytic H₂ evolution under UV–vis light. As a proof of concept, herein, it is demonstrated that 3D-printed MOF-derived monolith photocatalysts show five times higher H₂ evolution performance compared with TiO₂/C powder sample due to better interaction between 3D-printed photocatalysts and the incident light. The high surface area, the formation of hierarchical macro- to nanopores, and the optimizable shape/size of the 3D-printed catalyst maximize the exposure of catalytic active sites to incident photons and increase their photocatalytic H₂ evolution performance. In addition, the N-functionalized porous carbon from organic linker, and the uniformly distributed Pt/PtO_x species deposited by ALD, provide cocatalytic active sites for photocatalytic reaction and further enhance photocatalytic activity 30% of 3D-printed monoliths. This work on the 3D-printed MOF-derived free-standing monoliths for photocatalytic application provides a readily available approach to further fabricate a variety of 3D-printed MOF-based and derived materials for different energy and environment applications.

Bimetal-organic-framework (Bi-MOF) NH2-MIL-125(Ti/Cu)-derived nanocomposites are systematically investigated to elucidate the role of individual species TiO2, CuxO and the porous carbon matrix in photocatalytic activity. Among the studied samples, the TiO2/CuxO/C nanocomposite derived from heat processing NH2-MIL-125(Ti/Cu) under Ar/H2O vapor demonstrates the highest photocatalytic H2 evolution performance due to the formation of a phasejunction between the well-crystallized anatase/rutile TiO2 polymorph, the optimized and codoped nitrogen/carbon in the composites, the formation of p-n heterojunctions between the TiO2 and CuxO nanoparticles, as well as their uniform distribution in a hydrophilic porous carbon matrix decorated with N and carboxylic functional groups. These parameters enable the in situ-formed multi-heterostructures in these nanocomposites to not only possess relatively narrower energy band gaps and improved spatial charge separation due to the formed type-II staggered p-n heterojunctions but also offer multiple pathways for charge diffusion, resulting in lower charge-transfer resistance, suppressed bulk charge recombination, and consequently, much improved visible-light absorption. Therefore, the Bi-MOF NH2-MIL-125(Ti/Cu)-derived TiO2/CuxO/C nanocomposite provides easily accessible active sites with an excellent photocatalytic H2 evolution activity of 3147 μmol gcat-1 h-1, 99 times higher than that of bare TiO2. This work provides a simple one-step approach to producing tunable novel nanocomposites for efficient photocatalytic H2 evolution without using expensive noble metals as cocatalysts.