Transition metals supported on carbons play an important role in catalysis and energy storage. By pyrolysis of metal alginate, highly active catalysts for the Fischer-Tropsch synthesis (FTS) can be produced. However, the evolution of the carbon (alginate) and transition metal (Fe³⁺) during pyrolysis remains largely unknown and was herein corroborated with several advanced in situ techniques. Initially, Fe³⁺ was reduced to Fe²⁺, while bound to alginate. FeO nucleated above 300 °C, destabilizing the alginate functional groups. Increasing temperatures improved carbonization of the carbon support, which facilitated reduction of FeO to α-Fe at 630 °C. Catalysts were produced by pyrolysis between 400 and 700 °C, where the highest FTS activity (612 µmol_CO g_Fe⁻¹ s⁻¹) was achieved for the sample pyrolyzed at low temperature. Lower metal loading, due to less decomposition of alginate, moderated sintering and yielded larger catalytic surface areas. The results provide valuable knowledge for rational design of metal-alginate-based materials.

@en

The fundamentals of structure sensitivity and promoter effects in the Fischer–Tropsch synthesis of lower olefins have been studied. Steady state isotopic transient kinetic analysis, switching 12CO to 13CO and H2 to D2, was used to provide coverages and residence times for reactive species on supported iron carbide particles of 2–7 nm with and without promoters (Na + S). CO coverages appeared to be too low to be measured, suggesting dissociative adsorption of CO. Fitting of CH4 response curves revealed the presence of parallel side-pools of reacting carbon. CHx coverages decreased with increasing particle size, and this is rationalized by smaller particles having a higher number of highly active low coordination sites. It was also established that the turnover frequency increased with CHx coverage. To calculate H coverages, new equations were derived to fit HD response curves, again leading to a parallel side-pool model. The H coverages appeared to be lower for bigger particles. The H coverage was suppressed upon addition of promoters in line with lower methane selectivity and higher lower olefin selectivity. Density functional theory (DFT) was applied on H adsorption for a fundamental understanding of this promoter effect on the selectivities, with a special focus on counterion effects. Na2S is a better promoter than Na2O due to both a larger negative charge donation and a more effective binding configuration. On the unpromoted Fe5C2 (111) surface, H atoms bind preferably on C after dissociation on Fe. On Na2S-promoted Fe5C2 surfaces, adsorption on carbon sites weakens, and adsorption on iron sites strengthens, which fits with lower H coverage, less CH4 formation, and more olefin formation.@en