Shape memory polymer composites based on a blend of thermoplastic polyurethane (TPU) segmented block copolymer and poly(ε-caprolactone) (PCL) with weight ratio of 70/30 and various nanomagnetite contents (0–5 wt%) were prepared by melt blending of TPU and PCL, together with a masterbatch of TPU/nanomagnetite. The samples were compounded for 10 min at 200 °C using an internal mixer. Synthesized nanomagnetite powder was introduced to the masterbatch via a solution mixing method using a high-intensity ultrasonic horn. Subsequently, thermal, mechanical, rheological and electrical properties of the TPU/PCL/nanomagnetite shape memory composites were investigated through various tests. The degree of crystallization of the PCL component in the composite structure was inspected by differential scanning calorimetry (DSC) and X-ray diffraction measurements. The results revealed that the percentage of crystallinity and the melting temperature of the PCL component changed in the presence of magnetite nanoparticles, which was related to the nanoparticles acting as nucleants. Observing a single glass transition temperature (T g) in DSC thermograms of the samples was indicative of good compatibility of the TPU and PCL components in the composite structure. This was also confirmed by dynamic-mechanical analysis in which the loss modulus curves showed a single glass transition temperature. Moreover, the loss modulus peak at glass transition was lowered and broadened by addition of nanomagnetite, by which it was assumed that introducing nanoparticles into the system changed the mechanism of glass transition due to particle–matrix interactions. The dynamic rheological and electrical resistivity experiments verified the existence of a low percolation threshold at about 2 wt% nanomagnetite. The state of nanomagnetite dispersion in the masterbatch and the microstructure of the ternary composites were characterized by scanning electron microscopy. Finally, adding nanomagnetite led to weakening of shape recovery of the polymer blend, with shape recovery dropping to 70 % at 5 % of nanomagnetite.@en

Recent studies on inorganic/polymer nanocomposites have shown enhancements in thermal, mechanical, and chemical properties over the neat polymer without compromising density, toughness, and processibility. When nanoparticles are incorporated into the polymer matrix, significant enhancements in thermal and mechanical properties of the nanocomposite are observed. The present study is focused on the preparation and characterization of nanosize magnetite-reinforced PU composites, which induces magnetic properties to a specific thermoplastic polyurethane elastomer. The nanocomposites are prepared and the effects of magnetite content on thermal, mechanical, and magnetic properties of the nanocomposites are evaluated. Ultrasonication was used to disperse the nanoparticles and break up any large clumps and aggregates and followed by mechanical mixing. The magnetic nanocomposites were characterized by FT-IR spectroscopy, thermogravimetric analysis (TGA), scanning electron microscopy (SEM), and vibrating sample magnetometry (VSM). Characterization of the magnetic nanocomposite by FT-IR showed a successful incorporation of magnetite nanoparticles into the polymeric matrix. TGA and magnetometry of the magnetic nanocomposites revealed the amount of magnetite that was incorporated into the polymeric phase. Finally, the corresponding magnetization behavior of the nanocomposites was studied.@en