Ordered layered structures serve as essential components in lithium (Li)-ion cathodes^1–3. However, on charging, the inherently delicate Li-deficient frameworks become vulnerable to lattice strain and structural and/or chemo-mechanical degradation, resulting in rapid capacity deterioration and thus short battery life^2,4. Here we report an approach that addresses these issues using the integration of chemical short-range disorder (CSRD) into oxide cathodes, which involves the localized distribution of elements in a crystalline lattice over spatial dimensions, spanning a few nearest-neighbour spacings. This is guided by fundamental principles of structural chemistry and achieved through an improved ceramic synthesis process. To demonstrate its viability, we showcase how the introduction of CSRD substantially affects the crystal structure of layered Li cobalt oxide cathodes. This is manifested in the transition metal environment and its interactions with oxygen, effectively preventing detrimental sliding of crystal slabs and structural deterioration during Li removal. Meanwhile, it affects the electronic structure, leading to improved electronic conductivity. These attributes are highly beneficial for Li-ion storage capabilities, markedly improving cycle life and rate capability. Moreover, we find that CSRD can be introduced in additional layered oxide materials through improved chemical co-doping, further illustrating its potential to enhance structural and electrochemical stability. These findings open up new avenues for the design of oxide cathodes, offering insights into the effects of CSRD on the crystal and electronic structure of advanced functional materials.

Layered O3-type oxides are one of the most promising cathode materials for Na-ion batteries owing to their high capacity and straightforward synthesis. However, these materials often experience irreversible structure transitions at elevated cutoff voltages, resulting in compromised cycling stability and rate performance. To address such issues, understanding the interplay of the composition, structure, and properties is crucial. Here, we successfully introduced a P-type characteristic into the O3-type layered structure, achieving a P3-dominated solid-solution phase transition upon cycling. This modification facilitated a reversible transformation of the O3-P3-P3′ structure with minimal and gradual volume changes. Consequently, the Na_0.75Ni_0.25Cu_0.10Fe_0.05Mn_0.15Ti_0.45O₂ cathode exhibited a specific capacity of approximately 113 mAh/g, coupled with exceptional cycling performance (maintaining over 70% capacity retention after 900 cycles). These findings shed light on the composition-structure-property relationships of Na-ion layered oxides, offering valuable insights for the advancement of Na-ion batteries.

One of the primary challenges to improving lithium-ion batteries lies in comprehending and controlling the intricate interphases. However, the complexity of interface reactions and the buried nature make it difficult to establish the relationship between the interphase characteristics and electrolyte chemistry. Herein, we employ diverse characterization techniques to investigate the progression of electrode-electrolyte interphases, bringing forward opportunities to improve the interphase properties by what we refer to as high-entropy solvation disordered electrolytes. Through formulating an electrolyte with a regular 1.0 M concentration that includes multiple commercial lithium salts, the solvation interaction with lithium ions alters fundamentally. The participation of several salts can result in a weaker solvation interaction, giving rise to an anion-rich and disordered solvation sheath despite the low salt concentration. This induces a conformal, inorganic-rich interphase that effectively passivates electrodes, preventing solvent co-intercalation. Remarkably, this electrolyte significantly enhances the performance of graphite-containing anodes paired with high-capacity cathodes, offering a promising avenue for tailoring interphase chemistries.

Improving the reversibility of lithium metal batteries is one of the challenges in current battery research. This requires better fundamental understanding of the evolution of the lithium deposition morphology, which is very complex due to the various parameters involved in different systems. Here, we clarify the fundamental origins of lithium deposition coverage in achieving highly reversible and compact lithium deposits, providing a comprehensive picture in the relationship between the lithium microstructure and solid electrolyte interphase (SEI) for lithium metal batteries. Systematic variation of the salt concentration offers a framework that brings forward the different aspects that play a role in cycling reversibility. Higher nucleation densities are formed in lower concentration electrolytes, which have the advantage of higher lithium deposition coverage; however, it goes along with the formation of an organic-rich instable SEI which is unfavorable for the reversibility during (dis)charging. On the other hand, the growth of large deposits benefiting from the formation of an inorganic-rich stable SEI is observed in higher concentration electrolytes, but the initial small nucleation density prevents full coverage of the current collector, thus compromising the plated lithium metal density. Taking advantages of the paradox, a nanostructured substrate is rationally applied, which increases the nucleation density realizing a higher deposition coverage and thus more compact plating at intermediate concentration (∼1.0 M) electrolytes, leading to extended reversible cycling of batteries.