The current paper analyses the mechanical and fracture behaviour of a High-Performance Fibre Reinforced Concrete (HPFRC). An HPFRC was developed in a previous stage aiming to simultaneously, maximise aggregates content, achieve a compressive strength of 90–120 MPa and maintaining self-compactability (SF1+VS2). The benefits of fibres hybridisation (using fibres with lengths of 13, 35 and 60 mm) on flexural strength are investigated using the wedge-splitting test, in order to achieve the highest performance while keeping a relatively low fibre content. The final selected mixture was characterised in terms of workability, compressive strength and modulus of elasticity. Six notched prismatic specimens were subjected to three-point bending tests, according to EN 14651, for classification according to the MC2010. Based on the bending tests data, the simplified linear characteristic tensile stress vs. crack opening displacement relationship of the HPFRC was evaluated according to MC2010 and two other analytical approaches available in the literature.

Fibre-reinforced cementitious materials represent one of the most significant developments in the field of concrete technology of the last decades. The improved performance of this new class of materials (in terms of workability, compressive strength, flexural/tensile behaviour and/or durability) allows rethinking several of the existing structural solutions. This paper describes research on high-performance fibre reinforced concrete (HPFRC) to be used at the slab-column connection zones of flat slabs, in order to improve its punching shear resistance. Design of Experiments (DoE) approach was used to design HPFRC paste and aggregate particle phases. As such, a central composite design was carried out to mathematically model the influence of mixture parameters and their coupled effects on deformability, viscosity and compressive strength. After that, a numerical optimization technique was applied to the derived models to select the best mixture, which simultaneously, maximizes aggregates content and allows achieving a compressive strength of 90–120 MPa, while maintaining self-compactability (SF1 + VS2), incorporating 1% steel fibres content.