Singlet fission in tetracene generates two triplet excitons per absorbed photon. If these triplet excitons can be effectively transferred into silicon (Si), then additional photocurrent can be generated from photons above the bandgap of Si. This could alleviate the thermalization loss and increase the efficiency of conventional Si solar cells. Here, we show that a change in the polymorphism of tetracene deposited on Si due to air exposure facilitates triplet transfer from tetracene into Si. Magnetic field-dependent photocurrent measurements confirm that triplet excitons contribute to the photocurrent. The decay of tetracene delayed photoluminescence was used to determine a transfer efficiency of ∼36% into Si. Our study suggests that control over the morphology of tetracene during the deposition will be of great importance to boost the triplet transfer yield further.

Carrier multiplication (CM) generates multiple electron-hole pairs in a semiconductor from a single absorbed photon with energy exceeding twice the band gap. Thus, CM provides a promising way to circumvent the Shockley-Queisser limit of solar cells. The ideal material for CM should have significant overlap with the solar spectrum and should be able to fully utilize the excess energy above the band gap for additional charge carrier generation. We report efficient CM in mixed Sn/Pb halide perovskites (band gap of 1.28 eV) with onset just above twice the band gap. The CM rate outcompetes the carrier cooling process leading to efficient CM with a quantum yield of 2 for photoexcitation at 2.8 times the band gap. Such efficient CM characteristics add to the many advantageous properties of mixed Sn/Pb metal halide perovskites for photovoltaic applications.