Fused Filament Fabrication is a promising manufacturing technology for the circularity of space missions. Potential scenarios include in-orbit applications to maximize mission life and to support long-term exploration missions with in situ manufacturing and recycling. However, its adoption is restricted by the availability of engineering polymers displaying mechanical performance combined with resistance to space conditions. Here, a thermotropic Liquid Crystal Polymer (LCP) is reported as a candidate material with extrusion 3D printing. To expand its scope of applicability to structural parts for space applications, four different exposure conditions are studied: thermal cycling under vacuum, atomic oxygen, UV, and electron irradiations. While 1 MeV-electron irradiation leads to a green coloration due to annealable color centers, the mechanical performance is only slightly decreased in dynamic mode. It is also found that increased printing temperature improves transverse strength and resistance to thermal cycling with the trade-off of tensile stiffness and strength. Samples exposed to thermal cycling and the highest irradiation dose at lower printing temperatures still display a Young's modulus of 30 GPa and 503 MPa of tensile strength which is exceptionally high for a 3D-printed polymer. For the types of exposure studied, overall, the results indicate that LCP 3D-printed parts are well suited for space applications.@en

Anisotropic materials formed by living organisms possess remarkable mechanical properties due to their intricate microstructure and directional freedom. In contrast, human-made materials face challenges in achieving similar levels of directionality due to material and manufacturability constraints. To overcome these limitations, an approach using 3D printing of self-assembling thermotropic liquid crystal polymers (LCPs) is presented. Their high stiffness and strength is granted by nematic domains aligning during the extrusion process. Here, a remarkably wide range of Young's modulus from 3 to 40 GPa is obtained during by utilizing directionality of the nematic flow during the printing process. By determining a relationship between stiffness, nozzle diameter, and line width, a design space where shaping and mechanical performance can be combined is identified. The ability to print LCPs with on-the-fly width changes to accommodate arbitrary spatially varying directions is demonstrated. This unlocks the possibility to manufacture exquisite patterns inspired by fluid dynamics with steep curvature variations. Utilizing the synergy between this path-planning method and LCPs, functional objects with stiffness and curvature gradients can be 3D-printed, offering potential applications in lightweight sustainable structures embedding crack-mitigation strategies. This method also opens avenues for studying and replicating intricate patterns observed in nature, such as wood or turbulent flow using 3D printing.

@en